Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Recommended Printing Conditions
Value | Units | Test Method / Conditions | |
Tensile Strenght at Break (50 mm/min.) | 70.0 | MPa | ASTM D638 |
Elongation At Break (50 mm/min.) | min. 30 | % | ASTM D638 |
Bending Stress (1.3 mm/min.) | 80.0 | MPa | ASTM D790 |
Flexural Modulus (1.3 mm/min.) | 2500.0 | MPa | ASTM D790 |
Impact Strength (Notched (23°C - 3.2 mm) | min. 40 | J/m | ASTM D256 |
Impact Strength (Notched (20°C - 3.2 mm) | min. 20 | J/m | ASTM D256 |
Rockwell Hardness | 80.0 | Scala R | ASTM D785 |
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.43 | g/cm3 | ASTM D792 |
Water Adsorption (24h - 23°C) | 0.1 | % | ASTM D570 |
Linear Mould Shrinkage | 1.0 - 1.8 | % | — |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature (1.82 MPa) | min. 70 | °C | ASTM D648 |
Vicat Softening Point (49N x 120°C/h) | min. 180 | °C | ASTM D1525 |
Continuos Exercise Temperature (120h) | 90.0 | °C | — |
Value | Units | Test Method / Conditions | |
Dielectric Costant (1MHz - secco) | 3.4 | — | IEC 60250 |
Dielectric Strenght (S=1mm) | 30.0 | KV/mm | IEC 60243-1 |
Volume Resistivity (Secco) | min. 10^15 | Ohm-cm | IEC 60093 |
Value | Units | Test Method / Conditions | |
Glow Wire Test (S=2 mm) | 960.0 | °C | IEC 695-2-1 |
Flammability (S=1.6 mm) | V0 | Classe | UL 94 |
Flammability (S=3.2 mm) | V0 | Classe | UL 94 |
Value | Units | Test Method / Conditions | |
Cylinder Temperature | 220 - 280 | °C | — |
Mold Temperature | 60 - 90 | °C | — |
Dry Temperature (2-4 h) | 90.0 | °C | — |
Injection Speed | Medio-alta | — | — |
Regulatory & Compliance
- Certifications & Compliance