LNP THERMOCOMP™ Compound - WX05502 - SABIC's Specialty

Identification & Functionality

Additives Included: Flame Retardant,
Heat Stabilizer,
Metal Deactivator
Chemical Family: Polyesters
Fillers Included: Glass Fiber,
Glass/Mineral,
Mineral,
Talc
Polymer Name: Polybutylene Terephthalate (PBT)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polyesters & Copolyesters

Features & Benefits

Materials Features: Cost Effective,
Flame Retardant,
Heat Stabilized,
High Stiffness,
Low Warpage

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Electrical Components,
Electrical/Electronic Applications,
Food Preparation Equipment,
Garden Equipment,
Home Appliances,
Lawn Equipment,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 V0
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	90	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.4	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	13240	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	141	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	10900	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	85	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	1.2	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11740	MPa	ISO 527
Flexural Stress ¹¹	142	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	11380	MPa	ISO 178

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.81	—	ASTM D792
Density ¹¹	1.8	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.02	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.3 - 0.5	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.03	%	ISO 62

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	221	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	205	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000021	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.00005	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	217	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	197	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	140	°C	UL 746B

	Value	Units	Test Method / Conditions
Comparative Tracking Index (UL, PLC) ¹¹	2	PLC Code	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 3) ¹¹	min. 0.75	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 0.75	mm	UL 746A
High Ampere Arc Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 3) ¹¹	min. 3	mm	UL 746A
High Voltage Arc Track Rate (PLC) ¹¹	0	PLC Code	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	5	PLC Code	ASTM D495

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	337	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	18	J/m	ASTM D256
Multi-Axial Impact ¹¹	1	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	8	J	ASTM D3763
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	22	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 0.75	mm	UL 94
UV-light (Water exposure/immersion) ᵖ	F2	—	UL 746C

Regulatory & Compliance

Packaging & Availability

LNP™ THERMOCOMP™ Compound WX05502