Starex HF-3201M

Identification & Functionality

Chemical Family

Polycarbonate (PC)

Fillers Included

Glass Fiber

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Features & Benefits

Materials Features

General Purpose

Applications & Uses

Markets

Consumer Goods

Applications

Consumer Goods — Appliances & Electronics

Plastics & Elastomers End Uses

Appliances

Properties

Flame Rating

UL 94 V0,

UL 94 V1

Filler

Glass Fiber

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength at Yield (5 mm/min)	100	MPa	ISO 527
Tensile Strength at Break (5 mm/min)	100	MPa	ISO 527
Tensile Modulus (5 mm/min)	5000	MPa	ISO 527
Tensile Strain at Break (5 mm/min)	4	%	ISO 527-2/1A
Flexural Strength (2 mm/min)	150	MPa	ISO 178
Flexural Modulus (2 mm/min)	5000	MPa	ISO 178
Charpy Impact Strength - V-notched (23°C, 4mm)	16	kJ/m2	ISO 179 1eA
Notched Izod Impact Strength (23°C, 4 mm)	13	kJ/m2	ISO 180 1A

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity (Natural or representative color)	1.33	-	ISO 1183
Melt Flow Index - MFI (250°C/10 kg)	11	g/10 min	ISO 1133
Molding Shrinkage - MD (Flow at 2mm)	0.1 ~ 0.3	%	ISO 294-4
Molding Shrinkage - TD (Cross-Flow at 2mm)	0.1 ~ 0.3	%	ISO 294-4

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm)	141	°C	ISO 75-2
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm)	145	°C	ISO 75-2
RTI, Ele (1.5, V-1)	80	°C	UL 746B
RTI, Imp (1.5, V-1)	80	°C	UL 746B

Regulatory & Compliance

Certifications & Compliance

UL 94