LNP LUBRILOY™ Compound - DF2041 - SABIC's Specialty - PC

Identification & Functionality

Additives Included: Flame Retardant,
Impact Modifier,
Lubricant (Unspecified),
Mold Release Agent,
Proprietary
Chemical Family: Polycarbonate (PC)
Fillers Included: Glass Fiber
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Materials Features: Flame Retardant,
Friction Resistant,
Good Mold Release,
Impact Modified,
Lubricated,
Non-brominated,
Non-chlorinated,
Wear Resistant
Lubriloy Compounds Feature: Improved impact over PTFE filled materials

Lower mold deposits

Excellent surface finish & colorability

Lower S.G. vs. PTFE filled materials

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cash Dispenser (ATM),
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Garden Equipment,
Home Appliances,
Lawn Equipment,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Ticket Machine,
Turf Applications,
Windows,
Wireless Communication
Plastics & Elastomers Processing Methods: Injection Molding
Applications: PC based LUBRILOY alloys are widely used in consumer electronics and medical applications for combination of low wear and friction, tight dimensional tolerances and nonhalogenated FR systems. They have also been used in automotive interiors for BSR reduction.

Properties

Flame Rating: UL 94 V0,
UL 94 V1,
UL 94 V2
Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Density ¹¹	1.33	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.06	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.18	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.39	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.4	%	ASTM D955
Wear Factor Washer ¹¹	57	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.43	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.36	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.11	%	ISO 62

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	92	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	102	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	603	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	154	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	11	J	ASTM D3763
Multi-Axial Impact ¹¹	3	J	ISO 6603
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	36	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	9	kJ/m²	ISO 180/1A

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 3	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ᵖ	min. 0.8	mm	UL 94
UL Recognized (94V-2 Flame Class Rating) ᵖ	min. 0.4	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ LUBRILOY™ Compound DF2041