Products

PRF Composite Materials RP800 is an epoxy tooling prepreg system capable of withstanding temperatures up to 190°C after full post cure. RP800 is available in carbon and glass woven fabrics from 200 - 800 g/m2 impregnated with epoxy resin. RP800 prepreg allows high quality tooling laminates to be produced directly from a low temperature master model permitting a wide choice of master model materials. Using a low temperature vacuum bag and autoclave process for inital cure, the tool laminate can then be demoulded for freestanding post cure.

PRF Composite Materials RP522 is made up of Woven fabrics which is used for General and Industrial Purpose.

PRF Composite Materials RP442 is designed to give an initial cure at low temperatures with enhanced toughness and higher service temperature, giving great flexibility in component manufacture. The system also has a longer out life for a low temperature system: up to 30 days at 20°C. RP442 can be supplied on a variety of PRF’s high quality reinforcement fabrics.

PRF Composite Materials RP802 is an epoxy tooling prepreg system capable of withstanding temperatures up to 190°C after full post cure. RP-802 is available in carbon and glass woven fabrics from 200 - 800 g/m2 impregnated with epoxy resin. RP-802 prepreg allows high quality tooling laminates to be produced directly from a low temperature master model permitting a wide choice of master model materials. Using a low temperature vacuum bag and autoclave process for inital cure, the tool laminate can then be demoulded for freestanding post cure.

PRF Composite Materials RP542-3 is a winter version of our popular RP542-1 component prepreg, providing a controlled flow, toughened epoxy prepreg system formulated for the manufacture of high performance structural composite parts requiring very good impact strength properties. The system has been formulated for a medium temperature cure of 90 - 120°C under vacuum or autoclave pressure and is also suitable for press molding. Fully cured, this system has a dry service temperature capability up to 120°C. The component surface finish with this system is excellent. The high tack level of this system is ideal for use in cold weather conditions, where temperatures in workshops drop below 15°C. The out life of the system is up to 40 days at 20°C, making this system suitable for the manufacture of large composite components. RP542-3 can be supplied on most of the vast range of PRF reinforcement materials in widths up to 1350 mm wide.

PRF Composite Materials RP801 is an epoxy tooling prepreg system capable of withstanding temperatures up to 190°C after full post cure. RP801 is available in carbon and glass woven fabrics from 200 - 800 g/m2 impregnated with epoxy resin. RP-801 prepreg allows high quality tooling laminates to be produced directly from a low temperature master model permitting a wide choice of master model materials. Using a low temperature vacuum bag and autoclave process for inital cure, the tool laminate can then be demoulded for freestanding post cure.

PRF Composite Materials RP803 is formulated to provide an initial cure cycle of either 12 hours at 60°C or 6 hours at 70°C and extended out life of 9 days at 20°C. The system is capable of withstanding temperatures up to 190°C after full post cure. RP803 is available in carbon and glass woven fabrics from 200 - 800 g/m2 impregnated with epoxy resin. RP803 prepreg allows high quality tooling laminates to be produced directly from a low temperature master model permitting a wide choice of master model materials. Using a low temperature vacuum bag and autoclave process for inital cure, the tool laminate can then be demoulded for freestanding post cure.

PRF Composite Materials RP542-4 is a controlled flow, toughened epoxy prepreg system formulated for the manufacture of high performance structural composite parts requiring very good impact strength properties. The system has been formulated for a medium temperature cure of 80 - 120°C under vacuum or autoclave pressure and is also suitable for press molding. Fully cured, this system has a dry service temperature capability up to 120°C. The component surface finish with this system is excellent. The tack level of this system has been optimized to meet the constructor’s requirements and will be retained for up to 60 days at 20°C making this system suitable for the manufacture of large composite components. RP-542-4 can be supplied on most of the vast range of PRF reinforcement materials in widths up to 1350 mm wide.

PRF Composite Materials RP542-1 is a controlled flow, tough epoxy prepreg system formulated for the manufacture of high performance structural composite parts requiring very good impact strength properties. The system has been formulated for a medium temperature cure of 80 - 120°C under vacuum or autoclave pressure and is also suitable for press molding. Fully cured, this system has a dry service temperature capability up to 120°C. The component surface finish with this system is excellent. The tack level of this system can be adjusted to meet the constructor’s individual requirements and will be retained for up to 40 days at 22°C making this system suitable for the manufacture of large composite components. RP-542-1 can be supplied on most of the vast range of PRF reinforcement materials in widths up to 1350 mm wide.