Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Optical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 5 mm/min) | 96 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 5 mm/min) | 96 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 5 mm/min) | 6 | % | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) | 50 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) | 3510 | MPa | ASTM D638 |
Flexural Stress (Break, 1.3 mm/min, 50 mm span) | 159 | MPa | ASTM D790 |
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) | 155 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) | 3170 | MPa | ASTM D790 |
Tensile Stress (Yield, 5 mm/min) | 95 | MPa | ISO 527 |
Tensile Stress (Break, 5 mm/min) | 78 | MPa | ISO 527 |
Tensile Strain (Yield, 5 mm/min) | 8.5 | % | ISO 527 |
Tensile Strain (Break, 5 mm/min) | 16.8 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) | 3110 | MPa | ISO 527 |
Flexural Stress (Yield, at 2 mm/min) | 123 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) | 3080 | MPa | ISO 178 |
Ball Indentation Hardness (H358/30) | 1.40E+02 | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (on Tensile Bar, flow) | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage (flow, 3.2 mm) | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage (xflow, 3.2 mm) | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate (at 367°C, 6.6 kgf) | 15.5 | g/10 min | ASTM D1238 |
Water Absorption (at 23°C, saturated) | 1.75 | % | ISO 62-1 |
Moisture Absorption (at 23°C, 50% RH) | 0.6 | % | ISO 62 |
Melt Volume Rate (at 360°C, 5.0 kg) | 8 | cm³/10 min | ISO 1133 |
Density | 1.3 | g/cm³ | ISO 1183 |
Specific Gravity | 1.3 | — | ASTM D792 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (Rate B/50) | 242 | °C | ASTM D1525 |
Vicat Softening Temperature (Rate B/50) | 242 | °C | ISO 306 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) | 217 | °C | ASTM D648 |
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) | 237 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) | 230 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 150°C, flow) | 0.00005 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) | 0.00005 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at 23°C to 150°C, flow) | 0.00005 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 150°C, xflow) | 0.00005 | 1/°C | ISO 11359-2 |
Ball Pressure Test (at 123°C to 127°C) | Pass | — | IEC 60695-10-2 |
Vicat Softening Temperature (Rate B/120) | 238 | °C | ISO 306 |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) | 228 | °C | ISO 75/Af |
Relative Temperature Index (Electrical) ᵖ | 160 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ | 120 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ | 160 | °C | UL 746B |
Thermal Conductivity | 0.22 | W/m-°C | ASTM E1530 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index | 175 | V | IEC 60112 |
Relative Permittivity (1 kHz) | 3.41 | — | ASTM D150 |
Relative Permittivity (100 Hz) | 3.41 | — | ASTM D150 |
Dielectric Strength (in oil, at 3.2mm) | 17 | kV/mm | ASTM D149 |
Dissipation Factor (at 50/60 Hz) | 0.025 | — | IEC 60250 |
Dissipation Factor (at 100 Hz) | 0.008 | — | IEC 60250 |
Dissipation Factor (at at 1 kHz) | 0.001 | — | IEC 60250 |
Dissipation Factor (at at 1 MHz) | 0.007 | — | IEC 60250 |
Comparative Tracking Index (UL, PLC) | 3 | PLC Code | UL 746A |
Hot Wire Ignition (PLC 1) | min. 3 | mm | UL 746A |
Hot Wire Ignition (PLC 2) | min. 0.75 | mm | UL 746A |
High Ampere Arc Ignition (PLC 4) | min. 0.75 | mm | UL 746A |
Value | Units | Test Method / Conditions | |
Haze (at 2.54 mm) | 2 | % | ASTM D1003 |
Light Transmission (at 2.54 mm) | 58 | % | ASTM D1003 |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) | No break | J/m | ASTM D4812 |
Instrumented Dart Impact Total Energy (at 23°C) | 33 | J | ASTM D3763 |
Izod Impact (Notched, at 23°C) | 69 | J/m | ASTM D256 |
Izod Impact (Notched, at -30°C) | 74 | J/m | ASTM D256 |
Izod Impact (Unnotched, 80*10*4, at 23°C) | No break | kJ/m² | ISO 180/1U |
Izod Impact (Unnotched, 80*10*4, at -30°C) | No break | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) | 4 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -30°C) | 5 | kJ/m² | ISO 180/1A |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) | No break | kJ/m² | ISO 179/1eU |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) | No break | kJ/m² | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Back Pressure (Plastic Pressure) | 5 - 10 | MPa | — |
Drying Temperature | 150 | °C | — |
Drying Time | 4 - 6 | Hrs | — |
Drying Time (Cumulative) | 24 | Hrs | — |
Front - Zone 3 Temperature | 380 - 405 | °C | — |
Maximum Moisture Content | 0.02 | % | — |
Melt Temperature | 380 - 405 | °C | — |
Middle - Zone 2 Temperature | 370 - 395 | °C | — |
Mold Temperature | 140 - 180 | °C | — |
Nozzle Temperature | 375 - 400 | °C | — |
Rear - Zone 1 Temperature | 360 - 380 | °C | — |
Shot to Cylinder Size | 40 - 60 | % | — |
Vent Depth | 0.025 - 0.076 | mm | — |
Intake Throat temperature | 70 - 100 | °C | — |
Screw Speed (Circumferential speed) | max. 0.2 | m/s | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
Glow Wire Flammability Index (passes at 960°C) ᵖ | 3.2 | mm | IEC 60695-2-12 |
Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 850 | °C | IEC 60695-2-13 |
Oxygen Index (LOI) ᵖ | 45 | % | ISO 4589 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability