Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Processing Information (Extrusion Blow Molding)
- Impact Properties
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ² Extrusion blow Molding parameters are only mentioned as general guidelines.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 68 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 120 | % | ASTM D638 |
Tensile Modulus (at 50 mm/min) ¹¹ | 2350 | MPa | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 94 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 10.2 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (Rate B/50) ¹¹ | 157 | °C | ASTM D1525 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 138 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 128 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 120 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
High Voltage Arc Track Rate (PLC) ᵖ | 3 | PLC Code | UL 746A |
Comparative Tracking Index (UL, PLC) ᵖ | 2 | PLC Code | UL 746A |
High Ampere Arc Ignition (PLC 1) ᵖ | min. 1.5 | mm | UL 746A |
High Ampere Arc Ignition (PLC 3) ᵖ | min. 3 | mm | UL 746A |
Hot Wire Ignition (PLC 2) ᵖ | min. 3 | mm | UL 746A |
Hot Wire Ignition (PLC 3) ᵖ | min. 1.5 | mm | UL 746A |
Arc Resistance (Tungsten, PLC) ᵖ | 7 | PLC Code | ASTM D495 |
Value | Units | Test Method / Conditions | |
Drying Temperature ² | 120 | °C | — |
Drying Time ² | 2 - 4 | Hrs | — |
Maximum Moisture Content ² | 0.02 | % | — |
Minimum Moisture Content ² | 0.01 | % | — |
Melt Temperature (Parison) ² | 265 - 280 | °C | — |
Barrel - Zone 1 Temperature ² | 260 - 290 | °C | — |
Barrel - Zone 2 Temperature ² | 260 - 290 | °C | — |
Barrel - Zone 3 Temperature ² | 260 - 290 | °C | — |
Barrel - Zone 4 Temperature ² | 260 - 290 | °C | — |
Adapter - Zone 5 Temperature ² | 260 - 290 | °C | — |
Mold Temperature ² | 60 - 100 | °C | — |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 800 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 75 | J | ASTM D3763 |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |
UL Recognized (94V-2 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |