LNP™ ELCRIN™ 610001UiQ2

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer,

UV Stabilizer

Polymer Name

PC/PBT Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Recycled Polymers

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free,

Contains PCR Resin,

Recyclable,

Recycled,

Sustainable

Materials Features

Chemical Resistant,

Ductile,

Flame Retardant,

Good Aesthetics,

Good Colorability,

Good Flow,

Good Mechanical Properties,

Good Moldability,

Good Processability,

Good UV Stability,

Good Weather Stability,

Heat Stabilized,

High Ductility,

High Flow,

High Flowability,

High Impact Resistance,

High Rigidity,

Low Temperature Impact Resistance,

Non-brominated,

Non-chlorinated,

Pigmentable,

Recyclable,

UV Resistant,

UV Stabilized,

Unreinforced

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Industrial,

Personal Care,

Printing & Packaging

Applications

Automotive & Transportation — Automotive

Chassis & Brake,

Exterior & Body,

Interior

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Housings & Enclosures

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Exterior Parts,

Automotive Interior Parts,

Building Materials,

Chassis,

Computer Components,

Consumer Applications,

Containers,

Covers,

Electrical Components,

Electrical/Electronic Applications,

Electronic Components,

Enclosure,

Front Spoiler,

Garden Equipment,

Housings,

Industrial Applications,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Side Spoiler,

Spoilers,

Sporting Goods,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB,

UL 94 V0,

UL 94 V1

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.25	—	ASTM D792
Melt Flow Rate (at 265°C, 5.0 kgf) ¹¹	23	g/10 min	ASTM D1238
Density ¹¹	1.25	g/cm³	ISO 1183
Melt Volume Rate (at 265°C, 5.0 kg) ¹¹	20	cm³/10 min	ISO 1133
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.06	%	ISO 62-4
Water Absorption (at 23°C, 24hrs) ¹¹	0.11	%	ISO 62-1
Mold Shrinkage (flow) ᵍ ¹¹	0.6 - 0.8	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.6 - 0.8	%	SABIC method

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	55	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	54	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	120	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2170	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	85	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2260	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹	55	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	46	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	5	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	105	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2120	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	83	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2230	MPa	ISO 178

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	85	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	105	°C	ASTM D648
Vicat Softening Temperature (Rate B/50) ¹¹	114	°C	ASTM D1525
Vicat Softening Temperature (Rate B/120) ¹¹	115	°C	ASTM D1525
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000071	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000076	1/°C	ASTM E831
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	90	°C	ISO 75/Af
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	105	°C	ISO 75/Bf

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	800	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	342	J/m	ASTM D256
Izod Impact (Notched, at 0°C) ¹¹	700	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	60	J	ASTM D3763
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	50	J	ASTM D3763
Instrumented Dart Impact Peak Force (at 23°C) ¹¹	4500	N	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	58	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹	17	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at 0°C) ¹¹	44	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	60	kJ/m²	ISO 179/1eA
Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	18	kJ/m²	ISO 179/1eA
Charpy Impact (at 0°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	48	kJ/m²	ISO 179/1eA

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80 - 90	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Maximum Moisture Content ⁷	0.04	%	—
Melt Temperature ⁷	245 - 275	°C	—
Nozzle Temperature ⁷	245 - 275	°C	—
Front - Zone 3 Temperature ⁷	245 - 275	°C	—
Middle - Zone 2 Temperature ⁷	220 - 265	°C	—
Rear - Zone 1 Temperature ⁷	220 - 255	°C	—
Mold Temperature ⁷	60 - 80	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	40 - 70	rpm	—
Shot to Cylinder Size ⁷	30 - 80	%	—
Vent Depth ⁷	0.038 - 0.076	mm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 0.4	mm	UL 94
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 1.5	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ᵖ	min. 0.8	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America