LNP™ LUBRICOMP™ Compound DL002P

Identification & Functionality

Additives Included

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Polycarbonate (PC)

Fillers Included

PTFE

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Materials Features

Friction Resistant,

Good Mold Release,

Good Processability,

High Flowability,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Enclosure,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

White Goods & Small Appliances,

Windows,

Wireless Communication

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield) ¹¹	53	MPa	ASTM D638
Tensile Stress (Yield) ¹¹	54	MPa	ISO 527
Tensile Stress (Break) ¹¹	44	MPa	ASTM D638
Tensile Stress (Break) ¹¹	43	MPa	ISO 527
Tensile Strain (Yield) ¹¹	5.3	%	ASTM D638
Tensile Strain (Yield) ¹¹	5.6	%	ISO 527
Tensile Strain (Break) ¹¹	30.5	%	ASTM D638
Tensile Strain (Break) ¹¹	23.1	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	2450	MPa	ASTM D638
Flexural Stress ¹¹	82	MPa	ASTM D790
Flexural Stress ¹¹	85	MPa	ISO 178
Flexural Modulus ¹¹	2200	MPa	ASTM D790
Flexural Modulus ¹¹	2070	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	2460	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.25	g/cm³	ISO 1183
Density ¹¹	1.24	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.1	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ISO 294
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	13.5	cm³/10 min	ASTM D1238
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 1.2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 1.2	%	ISO 294
Wear Factor Washer ¹¹	97	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.28	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.17	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.2	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	120	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000666	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000667	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000072	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000733	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	123	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	106	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	34	J	ASTM D3763
Multi-Axial Impact ¹¹	74	J	ISO 6603
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	300 - 315	°C	—
Front - Zone 3 Temperature ⁷	310 - 320	°C	—
Middle - Zone 2 Temperature ⁷	305 - 315	°C	—
Rear - Zone 1 Temperature ⁷	295 - 305	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 