LNP LUBRICOMP™ Compound - KL201 - SABIC's Specialty

Identification & Functionality

Additives Included: Lubricant (PTFE),
Lubricant (Unspecified),
Mold Release Agent,
Proprietary
Fillers Included: PTFE
Polymer Name: Polyacetal Copolymer (POM)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polyacetals

Features & Benefits

Materials Features: Friction Resistant,
Good Mold Release,
Lubricated,
Unreinforced,
Wear Resistant

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Electronic Components,
Home Appliances,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications,
Windows
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Density ¹¹	1.4	g/cm³	ISO 1183
Density ¹¹	1.41	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.97	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	2.5 - 3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2.5 - 3	%	ASTM D955
Wear Factor Washer ¹¹	12	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.3	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.09	—	ASTM D3702 Modified: Manual

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	157	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	91	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000089	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000085	1/°C	ASTM E831
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	93	°C	ISO 75/Af

Packaging & Availability

LNP™ LUBRICOMP™ Compound KL201