LNP LUBRICOMP™ Compound - RFL22E - SABIC's Specialty

Identification & Functionality

Additives Included: Heat Stabilizer,
Lubricant (PTFE),
Lubricant (Unspecified),
Mold Release Agent
Chemical Family: Polyamides
Fillers Included: Glass Fiber,
PTFE
Polymer Name: Polyamide 66 (PA 66)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polyamides

Features & Benefits

Materials Features: Friction Resistant,
Good Mold Release,
Heat Stabilized,
Lubricated,
Wear Resistant

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Electronic Components,
Home Appliances,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications,
Windows,
Wiring Devices
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	95	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	4400	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	138	MPa	ISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹	4.7	%	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4500	MPa	ISO 178

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000042	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.0001	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	256	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	236	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

	Value	Units	Test Method / Conditions
Glow Wire Ignitability Temperature (at 2.0 mm) ¹¹	675	°C	IEC 60695-2-13

Packaging & Availability

LNP™ LUBRICOMP™ Compound RFL22E