LNP™ LUBRICOMP™ Compound RFL369

Identification & Functionality

Additives Included

Flame Retardant,

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

PTFE

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Flame Retardant,

Friction Resistant,

Good Mold Release,

High Stiffness,

UL Listed,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Automotive Gears,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	128	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11500	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	152	MPa	ISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹	2.5	%	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	8500	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Density ¹¹	1.74	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000042	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000078	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	253	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	225	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index ¹¹	375	V	IEC 60112

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	20	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	7	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	285 - 300	°C	—
Front - Zone 3 Temperature ⁷	290 - 300	°C	—
Middle - Zone 2 Temperature ⁷	290 - 290	°C	—
Rear - Zone 1 Temperature ⁷	270 - 280	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Compliant (94V-0 Flame Class Rating)	1	mm	UL 94 by SABIC-IP

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 