LNP™ LUBRICOMP™ Compound RFP36

Identification & Functionality

Additives Included

Heat Stabilizer,

Lubricant (PTFE),

Lubricant (Silicone),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

PTFE,

PTFE/Silicone,

Silicone

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Friction Resistant,

Good Mold Release,

Heat Stabilized,

High Stiffness,

Lubricated,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Healthcare & Pharma,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Consumer Goods — Luggage & Leather Goods

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Electronic Components,

Enclosure,

Heaters,

Home Appliances,

Medical Devices,

Oil/Gas Applications,

Personal Accessories,

Pool Covers,

Sporting Goods,

Suitcase,

Tablets,

Tarpaulins,

Turf Applications,

Windows,

Wiring Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Modulus (at 50 mm/min) ¹¹	10480	MPa	ASTM D638
Tensile Stress (Break, 5 mm/min) ¹¹	148	MPa	ISO 527
Tensile Stress (Break) ¹¹	133	MPa	ASTM D638
Tensile Stress (Break) ¹¹	135	MPa	ISO 527
Flexural Stress ¹¹	195	MPa	ASTM D790
Flexural Stress ¹¹	207	MPa	ISO 178
Tensile Strain (Break, 5 mm/min) ¹¹	3.9	%	ISO 527
Tensile Strain (Break) ¹¹	2.2	%	ISO 527
Tensile Strain (Break) ¹¹	2.1	%	ASTM D638
Flexural Modulus ¹¹	7580	MPa	ASTM D790
Flexural Modulus ¹¹	9400	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	211	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7000	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	9800	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Wear Factor Washer ¹¹	11	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.56	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.48	—	ASTM D3702 Modified: Manual
Density ¹¹	1.48	g/cm³	ASTM D792
Density ¹¹	1.48	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.78	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.21	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.97	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	1.22	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000025	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000113	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	236	°C	ISO 75/Af
Relative Temperature Index (Electrical) ¹¹	65	°C	UL 746B
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	233	°C	ASTM D648
Relative Temperature Index (Mechanical with impact) ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ¹¹	65	°C	UL 746B
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	80	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, at 23°C) ¹¹	779	J/m	ASTM D4812
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A
Izod Impact (Notched, at 23°C) ¹¹	138	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	7	J	ASTM D3763
Multi-Axial Impact ¹¹	5	J	ISO 6603

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	280 - 305	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	95 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 1.5	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Regional Availability

• Americas
• Asia
• Europe
• North America