LNP THERMOCOMP™ Compound - DX10311X - SABIC's Specialty

Identification & Functionality

Additives Included: Heat Stabilizer,
Impact Modifier,
Mold Release Agent
Chemical Family: Polycarbonate (PC)
Fillers Included: Glass Fiber
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polycarbonates

Features & Benefits

Materials Features: Cost Effective,
Good Mold Release,
Heat Stabilized,
High Ductility,
High Impact Resistance,
High Modulus,
High Stiffness,
Impact Modified

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Plastics & Elastomers End Uses: Building Materials,
Cell Phones,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Garden Equipment,
Lawn Equipment,
Personal Accessories,
Pool Covers,
Tablets,
Tarpaulins,
Turf Applications,
Windows,
Wireless Communication
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	114	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.5	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	8690	MPa	ASTM D638
Flexural Stress ¹¹	180	MPa	ASTM D790
Flexural Modulus ¹¹	7410	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	115	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.50E+00	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	8610	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	172	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	180	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7450	MPa	ISO 178

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	125	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000021	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000068	1/°C	ASTM E831

Packaging & Availability

LNP™ THERMOCOMP™ Compound DX10311X