LNP THERMOCOMP™ Compound - EFB26ER - SABIC's Specialty

Identification & Functionality

Additives Included: Mold Release Agent
Chemical Family: Polyetherimide (PEI),
Polyimides (PI)
Fillers Included: Glass Bead,
Glass Fiber,
PTFE
Polymer Name: Polyether Imide (PEI)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Cost Effective,
Easy To Mold,
Good Mold Release,
Good Moldability,
Good Processability,
High Stiffness,
High Temperature Resistance,
Low Warpage,
Very Good Heat Resistance

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Plastics & Elastomers End Uses: Building Materials,
Cell Phones,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Garden Equipment,
Lawn Equipment,
Personal Accessories,
Pool Covers,
Tablets,
Tarpaulins,
Turf Applications,
Windows
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	156	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	153	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	1.5	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.5	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	9000	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	190	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	190	MPa	ISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹	1.9	%	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	10400	MPa	ISO 178

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000015	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000035	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	206	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	6	kJ/m²	ISO 180/1A

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	150	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	360 - 365	°C	—
Rear - Zone 1 Temperature ⁷	345 - 355	°C	—
Middle - Zone 2 Temperature ⁷	355 - 365	°C	—
Front - Zone 3 Temperature ⁷	365 - 375	°C	—
Nozzle Temperature ⁷	390 - 400	°C	—
Mold Temperature ⁷	120 - 150	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed (Circumferential speed) ⁷	0.2 - 0.3	m/s	—
Vent Depth ⁷	0.025 - 0.076	mm	—