Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Processing Information (Profile Extrusion)
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage (flow) ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Specific Gravity ¹¹ | 1.13 | — | ASTM D792 |
| Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 4 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 8 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 20 | cm³/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 72 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 105 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2580 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 71 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 57 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 8 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2680 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 105 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2600 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 126 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | 125 | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate A/120) ¹¹ | 155 | °C | ISO 306 |
| Ball Pressure Test (approximate maximum) ¹¹ | 135 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 144 | °C | ISO 306 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 136 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 123 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 125 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 125 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 125 | °C | UL 746B |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Value | Units | Test Method / Conditions | |
| Barrel - Zone 1 Temperature | 200 - 230 | °C | — |
| Barrel - Zone 2 Temperature | 220 - 250 | °C | — |
| Barrel - Zone 3 Temperature | 240 - 270 | °C | — |
| Barrel - Zone 4 Temperature | 240 - 270 | °C | — |
| Calibrator Temperature | 50 - 80 | °C | — |
| Die Temperature | 240 - 270 | °C | — |
| Drying Temperature | 100 - 110 | °C | — |
| Drying Time | 3 - 4 | Hrs | — |
| Hopper Temperature | 40 - 60 | °C | — |
| Melt Temperature | 240 - 270 | °C | — |
| Value | Units | Test Method / Conditions | |
| Charpy Impact (Unnotched, at 23°C) ¹¹ | 18 | kJ/m² | ISO 179/2C |
| Izod Impact (Notched, at 23°C) ¹¹ | 220 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 16 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 0°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -10°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -20°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 105 | °C | — |
| Drying Time ⁷ | 3 - 4 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.02 | % | — |
| Melt Temperature ⁷ | 280 - 300 | °C | — |
| Front - Zone 3 Temperature ⁷ | 270 - 290 | °C | — |
| Nozzle Temperature ⁷ | 270 - 300 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 280 - 300 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C | — |
| Hopper Temperature ⁷ | 60 - 80 | °C | — |
| Mold Temperature ⁷ | 80 - 100 | °C | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2.5 | mm | UL 94 |
| UL Recognized (94-5VB Flame Class Rating) ʳ | min. 2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1 | mm | UL 94 |
| Glow Wire Flammability Index (at 1 mm) ʳ | 9.60E+02 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (passes at 960°C) ʳ | 1 | mm | IEC 60695-2-12 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability