Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁵ Typical values only. Variations within normal tolerances are possible for various colors. All values are measured at least after 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume rate are measured on injection molded samples. All samples are prepared according to ISO 294. Only typical data for material selection purpose.Not to be used for part or tool design. The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, Type I, 5 mm/min) ¹⁵ | 112 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹⁵ | 2.9 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) ¹⁵ | 5400 | MPa | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹⁵ | 163 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹⁵ | 5200 | MPa | ASTM D790 |
Hardness (Rockwell R) ¹⁵ | 121 | - | ASTM D785 |
Tensile Stress (Break, 5 mm/min) ¹⁵ | 90 | MPa | ISO 527 |
Tensile Stress (Break, 5 mm/min) ¹⁵ | 112 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹⁵ | 2.7 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹⁵ | 5500 | MPa | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹⁵ | 5600 | MPa | ISO 527 |
Flexural Stress (Yield, at 2 mm/min) ¹⁵ | 140 | MPa | ISO 178 |
Flexural Stress (Yield, at 2 mm/min) ¹⁵ | 163 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹⁵ | 4900 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹⁵ | 5200 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹⁵ | 1.21 | - | ASTM D792 |
Melt Flow Rate (at 300°C, 5.0 kgf) ¹⁵ | 20 | g/10 min | ASTM D1238 |
Melt Volume Rate (at 280°C, 10.0 kg) ¹⁵ | 17 | cm³/10 min | ISO 1133 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹⁵ | 0.5 | % | SABIC method |
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹⁵ | 0.38 | % | SABIC method |
Density ¹⁵ | 1.21 | g/cm³ | ISO 1183 |
Water Absorption (at 23°C, saturated) ¹⁵ | 0.2 | % | ISO 62-1 |
Moisture Absorption (at 23°C, 50% RH) ¹⁵ | 0.05 | % | ISO 62 |
Moisture Absorption (at 23°C, 50% RH) ¹⁵ | 0.11 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹⁵ | 153 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹⁵ | 154 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹⁵ | 153 | °C | ASTM D648 |
Vicat Softening Temperature (Rate B/120) ¹⁵ | 163 | °C | ISO 306 |
Vicat Softening Temperature (Rate B/50) ¹⁵ | 161 | °C | ISO 306 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹⁵ | 0.000038 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹⁵ | 0.000035 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹⁵ | 0.000064 | 1/°C | ISO 11359-2 |
Ball Pressure Test (at 123°C to 127°C) ¹⁵ | Pass | - | IEC 60695-10-2 |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹⁵ | 155 | °C | ISO 75/Af |
Relative Temperature Index (Electrical) ¹⁵ | 65 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ¹⁵ | 65 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ¹⁵ | 65 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index ʳ ¹¹ | 175 | V | IEC 60112 |
Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹⁵ | 500 | J/m | ASTM D256 |
Izod Impact (Notched, at 23°C) ¹⁵ | 72 | J/m | ASTM D256 |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹⁵ | 31 | kJ/m² | ISO 179/1eU |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹⁵ | 27 | kJ/m² | ISO 179/1eU |
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹⁵ | 7 | kJ/m² | ISO 179/1eA |
Izod Impact (Unnotched, at 23°C) ¹⁵ | 500 | J/m | ASTM D4812 |
Izod Impact (Unnotched, at -30°C) ¹⁵ | 500 | J/m | ASTM D4812 |
Izod Impact (Notched, at -30°C) ¹⁵ | 61 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy (at 23°C) ¹⁵ | 10 | J | ASTM D3763 |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹⁵ | 27 | kJ/m² | ISO 180/1U |
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹⁵ | 28 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹⁵ | 7 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -30°C) ¹⁵ | 6 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 110 - 120 | °C | - |
Drying Time ⁷ | 3 - 4 | Hrs | - |
Drying Time (Cumulative) ⁷ | 8 | Hrs | - |
Maximum Moisture Content ⁷ | 0.02 | % | - |
Melt Temperature ⁷ | 300 - 325 | °C | - |
Nozzle Temperature ⁷ | 300 - 325 | °C | - |
Front - Zone 3 Temperature ⁷ | 290 - 325 | °C | - |
Middle - Zone 2 Temperature ⁷ | 275 - 320 | °C | - |
Rear - Zone 1 Temperature ⁷ | 265 - 315 | °C | - |
Mold Temperature ⁷ | 80 - 110 | °C | - |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | - |
Screw Speed ⁷ | 20 - 100 | rpm | - |
Shot to Cylinder Size ⁷ | 30 - 70 | % | - |
Value | Units | Test Method / Conditions | |
Glow Wire Flammability Index (passes at 960°C) ʳ | 3.2 | mm | IEC 60695-2-12 |
UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.75 | mm | UL 94 |
UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability