Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Key Characteristics
Chemically crosslinkable, high density polyethylene for injection molding
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Appearance
- Pellets
- Mechanical Properties
- Physical Properties
- Thermo-Mechanical Properties
Value | Units | Test Method / Conditions | |
Elongation at Break | 450 | % | IEC 60811-501 |
Hot Set (40cm² / 200°C / Elongation) (Cure Assessment) | 60 | % | IEC 60811-2-1 |
Gel Content | 62 | % | ASTM D2765-11 |
Hot Set (40cm² / 200°C / Set) | 0 | % | IEC 60811-2-1 |
Tensile Strength (at Break) | 26 | N/mm² | IEC 60811-501 |
Value | Units | Test Method / Conditions | |
Density | 0.954 | g/cm³ | BS EN ISO 1183-3 |
Melt Flow Rate (at 190°C / 2.16kg) | 4.5 | g/10min | Internal Method |
Flexural Modulus (at 1% Secant) | 900 | N/mm² | ISO 527 |
Value | Units | Test Method / Conditions | |
Abrasion Resistance | 160 | mm³ | ISO 4649:2010 |
E.S.C.R. | 20 | Hours | ASTM D1693 (A) |
Izod Nothched Strength (at -30°C) | 5.99 | KJ/m² | ISO 180:2000 |
Izod Nothched Strength (at 23°C) | 12.27 | KJ/m² | ISO 180:2000 |
Technical Details & Test Data
- Processing
By conventional thermoplastic injection molding using temperatures set in the range 200°–250°C. It is essential to minimize molding stresses since these may be released during elevated temperature cure or service, causing warpage.
Crosslinking –In Hot Water at 95°- 100°C 1mm Thickness 5 Hours 2mm Thickness 12 Hours 3mm Thickness 24 Hours - Color Masterbatches
CM488/6 catalyst masterbatch is normally added at 5% to 95% of SX739 graft.
Addition of approved color masterbatches, including black, up to a maximum of 1%, has no detrimental effect on the properties or crosslinking capability.
It is recommended that all masterbatches, including those containing the catalyst, should be thoroughly dried at 60°C for 8 hours or at 80°C for 4 hours.
Packaging & Availability
- Packaging
The following possibilities are available:
- Moisture resistant sacks containing 25kg
- Boxes with a moisture resistant heat sealed liner containing approximately 500kg
Storage & Handling
- Storage & Shelf Life
SX739 normally has shelf life of at least 6 months from the date of manufacture. The storage of silane cross-linkable compounds in cool dry conditions will maximize useful shelf life. Other precautions are:
- Packaging should remain sealed
- Avoid temperatures above 35°C
- Avoid storage outside and in direct sunlight
- Use within 8 hours of opening packaging