Features & Benefits
- Materials Features
- Product Highlights
- Low mix viscosity
- High Tg
- Good wetting of the reinforcements
- Long Pot life
Applications & Uses
- Markets
- Composites Processing Methods
- Processing Conditions
- After mixing according to the indicated ratio, carry out impregnation of the reinforcements.
- To ensure an optimal use and a good impregnation, please use packagings stored at temperature above 15 ° C.
- The physical properties are guaranteed between 18°C and 25°C.
- Outside this range, variations in viscosity and reactivity will be observed.
Properties
- Color
- Component A
- Mechanical Properties
- Typical Properties
- Component B
| Value | Units | Test Method / Conditions | |
| Mix ratio by weight | 100 | — | — |
| Mix ratio by volume at 25°C | 100 | — | — |
| Aspect | Liquid | — | — |
| Viscosity at 25°C | 1600 | mPa.s | — |
| Specific Gravity at 25°C | 1.2 | g/cm³ | ISO 1675 : 1985 |
| Value | Units | Test Method / Conditions | |
| Tensile modulus at 23°C | 4600 | MPa | ISO 527 : 1993 |
| Tensile Strength at 23°C | 26 | MPa | ISO 527 : 1993 |
| Elongation at Break at 23°C | 1 | % | ISO 527 : 1993 |
| Flexural Modulus at 23°C | 2900 | MPa | ISO 178 : 1993 |
| Maximum flexural Strength at 23°C | 73 | MPa | ISO 178 : 1993 |
| Value | Units | Test Method / Conditions | |
| Aspect | Liquid | — | — |
| Viscosity at 25°C | 550 | mPa.s | BROOKFIELD LVT |
| Specific Gravity of cured product at 23°C | 1.15 | — | ISO 2781 : 1996 |
| Pot life at 25°C on 500 g | min. 400 | — | ASTM D 2471 - 99 |
| Time to reach 1,000 on 500g at 25°C | min. 230 | mPa.s | — |
| Value | Units | Test Method / Conditions | |
| Aspect | Liquid | — | — |
| Mix ratio by weight | 50 | — | — |
| Mix ratio by volume at 25°C | 63 | — | — |
| Viscosity at 25°C | 100 | mPa.s | — |
| Specific Gravity at 25°C | 0.95 | g/cm³ | ISO 1675 : 1985 |
Packaging & Availability
- Packaging
EPOLAM 2092 RESIN
- 19 KG
EPOLAM 2092 HARDENER
- 19 KG
Storage & Handling
- Handling
IMPORTANT : do not leave the mixing without any supervision. The exothermy discharge during the reaction on these quantities leads to an uncontrolled decomposition of the resin mixing. TOXIC SMOKES MAY APPEAR AND CAUSE PHYSICAL INJURIES. Small quantities of mixing reduce heat release. In case of uncontrolled reaction, the mixing has to be dipped into a water container.
Normal health and safety precautions should be observed when handling these products- Ensure good ventilation
- Wear gloves, safety glasses and waterproof clothes.
- Storage Conditions
EPOLAM 2092 RESIN
- 6 months at 15-25°C
- 12 months at -18°C
EPOLAM 2092 HARDENER
- 24 months at 15-25°C