3B Fiberglass 399 Direct Rovings consist of continuous filaments bonded into a single strand and wound onto a bobbin shape. A proprietary sizing applied on the fibers assures an excellent resin-to-glass bonding.Corrosion resistant 399 Direct Rovings made of Advantex® glassare specifically designed for pultrusion process and are compatible with thermosets resins. They are the materials of choice for the manufacturing of high quality profiles. 399 Direct Rovings made of Advantex® glass are also used in filament winding process under specific conditions; contact us for further assistance.

3B Fiberglass MF 01 ER are E-CR glass filaments ground to a specified density. MF 01 ER is designed to reinforce products like thermoplastics, thermoset resins, glues, coatings, and adhesives within a large range of applications and markets.MF 01 ER represents a main improvement compared to minerals when aiming for a higher stiffness and/or better impact properties in combination with specific properties, such as flow enhancement, flame retardancy, uniform isotropic shrinkage, resistance to acid environment, coating stability, etc. MF 01 ER can be collocated in between mineral fillers and most com-monly available milled fibers as it dis-plays an intermediate length/diameter aspect ratio. The product comes in a powdery form that provides both improved flowability/handling and low density.

3B Fiberglass DS 5163-13P chopped strand is spe-cifically designed for excellent per-formances in injection and transfer molding processes & applications.The sizing coated at the glass fiber surface is engineered for enhanced compatibility with phenolic and epoxy resin systems.Thanks to its very light color, this product can be used in any natural grade compounds without impacting the color of the final part.An innovative manufacturing techno-logy provides DS5163-13P chopped strand with an excellent strand inte-grity and bulk density. As a result this product exhibits excellent feeding properties with very low fuzz generation.

3B Fiberglass EM 1011 is a non-woven mat made from 3B E-CR glass filaments, consisting of chopped fibers randomly and yet evenly orien-tated. The 50 mm length chopped fibers are coated with silane coupling agent and are held together using emulsion binder. CSM is particularly suitable for hand lay-up process using thermoset resin systems to manufacture wide range of products for automobile, recreation, chemical, electrical industries.CSM EM1011 conforms to BS 14118 and IS 11551.

3B Fiberglass SE 4220 are corresponds to 3B’s portfolio of direct roving glassfi bre designed to rein-force polyolefi ns. Made out of E-CR glass, these direct roving fi bres consist of conti-nuous fi laments bonded together into a single strand and wound into a cylindrical shaped bobbin. SE 4220 (17μm) corresponds to an E-CR glass made direct roving whose strand consists of gathered 17μm diameter glass fi laments for reinforcing polyolefi ns. This 17μm fi lament diameter product offers the best compromise between mechanical performances and aptitude for knitting/weaving in the case of Continuous Fiber Thermoplastics manu-facturing. This is also the most common fi lament diameter in use for the production of LFT pellets or D-LFT parts. SE 4220 (17μm) is compatible with both polyethylene (PE) and polypropylene (PP).SE 4220 (17μm) direct roving is internal/inside pull and is available in 1200 tex and 2400 tex linear densities.

3B Fiberglass W 2020 are spe-cifically designed to provide signifi-cantly higher modulus, strength and enhanced fatigue performances ver-sus traditional E-glass for wind turbine blades made out of epoxy resin. HiPer-texTM W 2020 Rovings are per-fectly suited for the production of high modulus Non Crimped Glass Fabrics and prepregs. The sizing W 2020 is purposely formulated for excellent adhesion with epoxy resin systems and leads to superior interfibre and interlaminar shear strengths as well as dynamic performances. The specific boron free glass formula-tion provides superior hydrolysis and corrosion resistance. These properties improvements versus typical E-glass will help blade desi-gners to push further the limits of glass fiber blade designs, especially for the long blades required for the multi MW turbines for on shore and off shore. The W 2020 roving is approved by Germanischer Lloyd for the use in wind turbine rotor blades.

3B Fiberglass SE 3030 consist of conti-nuous filaments bonded into a single strand and wound onto a bobbin shape. A proprietary sizing applied on the fibers assures an excellent resin-to-glass bonding. SE 3030 Direct Rovings made of Advantex® glass are specifically desi-gned for multipurpose applications/processes such as the production of Non Crimped Fabrics, prepreg, filament winding, pultrusion, etc. The sizing of SE 3030 Direct Rovings is compatible with multiple resins: i.e. polyester, vinylester and epoxies. SE 3030 Direct Rovings present high level of fatigue performances, supe-rior interfibre and interlaminar shear strengths.

3B Fiberglass DS 2200-13P is a 13 μm filament dia-meter, 4 mm long chopped glass fiber designed for production of Polyolefin compounds.DS 2200-13P shows outstanding compatibility with Polypropylene. This is the material of choice for very high glass content (up to 50 %wt) compound grades that require good fiber dispersion as well as mechanical properties. DS 2200-13P is also desig-ned for parts weathering in prolonged contact with water, detergents and glycol. DS 2200-13P can also be used in applications complying with strin-gent requirements of food contact and drinkable water standards EC 10/2011, FDA, BfR and ACS. DS 2200-13P is supplied on a pel-letized form and offers outstanding feeding-to-extruder behavior as well as excellent fiber impregnation.DS 2200-13P’s sizing chemistry also requires reduced amount of coupling agents so that parts reach optimum mechanical performances.

3B Fiberglass R25H consist of continuous glass filaments bonded into a single strand and wound onto a bobbin shape. A proprietary sizing applied on the fibers assures excellent resin-to-glass bonding.Corrosion resistant R25H Direct Rovings made of Advantex® glass are specifically designed for filament winding processes (continuous or discontinuous) for the manufacturing of composite pipes. The silane sizing of R25H is designed for excellent adhesion to thermoset resins and is also drinking water contact approved. Also, combination of high temperature resistance of E-CR Advantex® glass and easy texturisation of R25H Direct Rovings make them ideal for muffler filling.R25H Direct Rovings made of Advantex® glass are also used in pultrusion or weaving-knitting processes under specific conditions; contact us for further assistance.

3B Fiberglass CR 6202 is a non-woven mat made from 3B E-CR glass filaments, consisting of chopped fibers randomly and yet evenly orien-tated. The 50 mm length chopped fibers are coated with silane coupling agent and are held together using emulsion binder. CSM is particularly suitable for hand lay-up process using thermoset resin systems to manufacture wide range of products for automobile, recreation, chemical, electrical industries.CSM EM1011 conforms to BS 14118 and IS 11551.

3B Fiberglass CM 1020 is a non-woven mat made out of E-CR glass filaments, consisting of continuous fibers randomly oriented in multiple layers. The glassfibre is bonded with a silane coupling agent and the layers held together with a suitable binder. The CM 1020 family products contain an insoluble binder compatible with a large range of thermoset matrices like both unfilled or filled unsaturated polyester (UP), vinyl ester (VE), epoxy (EP) and polyurethane (PU) resin systems.The CM 1020 powder mat is ideally suited for polyurethane foaming pro-cesses for the reinforcement of foam panels. The excellent mechanical pro-perties provided by 3B CFM combined with the good opening and the easy expansion of the CM 1020 mat during foam expansion make those reinforced R-PUF panels ideal for applications like thermal insulation of liquefied natural gas carrier and onshore storage.

3B Fiberglass M8615 is a non-woven mat made out of ECR glass _x005F_x001f_laments, consisting of continuous _x005F_x001f_bres randomly oriented in multiple layers. The glass _x005F_x001f_bre is bonded with a silane cou-pling agent and the layers held together with a suitable binder.The CFM products contain an insolublebinder compatible with both un_x005F_x001f_lled or _x005F_x001f_lled unsaturated polyester, vinyl ester, epoxy and polyurethane resin systems. The M8610 mat is ideally suited for injection molding, RTM and S-RIM processes for molding complex parts. The M8615mat version, with its high rigidity, helps to work with large CFM cuts without loosing _x005F_x001f_bres. The excellent mechanical properties provided by CFM combined with the good electrical properties of the resins make the molded parts attractive for applications like electrical apparatus (high voltage), transportation & automo-tive industries and infrastructuresequipments.

3B Fiberglass DS 1135-10N is designed to reinforce a broad range of polyamide resins, including PA6, PA66, PA610, PA6/66 copolymers and semi-aromatic PA. The product has been developed in order to help reinforced plastics to meet the requirements of the most common food contact and drinkable water norms (FDA, EC 10/2011, BfR and ACS).Its chemistry presents an excellent compatibility with flame retardant additives and impact modifiers.The performance in hydrolysis/glycolysis resistance is also very good.Therefore, the fiber is enhancing dry-as-molded and long-term properties, in a large range of natural and colored formulations.Finally, DS1135-10N is a multi-compatible chopped strand PA, with excellent strand integrity and bulk density.

3B Fiberglass CM 4020 is a non-woven mat made out of ECR glass _x005F_x001f_laments, consisting of continuous _x005F_x001f_bres randomly oriented in multiple layers. The glass _x005F_x001f_bre is bonded with a silane coupling agent and the layers held together with a suitable binder. The CFM products contain an insoluble binder compatible with both un_x005F_x001f_lled or _x005F_x001f_lled unsaturated polyester, vinyl, ester, epoxy and polyurethane resin systems. The CM 4020 mat is ideally suited for injection molding RTM and S-RIM processes. The CM 4020 mat has a high rigidity which helps to work with large CFM cuts without loosing _x005F_x001f_bres. The ex-cellent mechanical properties provided by CM 4020 combined with the good electrical properties of the resins make the molded parts attractive for applica-tions like the electrical apparatus (high voltage), transportation and automotive industries, infrastructures equipments.

3B Fiberglass DS 8800-11P is a glass chopped strand specifically designed to rein-force high performance thermoplastic polymers, including PPS, PES, PSU, PPSU, PEI and PEEK. Furthermore, it shows interesting benefits in reinfor-cing PBT resins. 3B’s state-of-the-art manufacturing technology provides to DS 8800-11P very good strand integri-ty and bulk density leading to smooth compounders feeding, with low fuzz generation. DS 8800-11P displays excellent dis-persion within a large range of resin viscosities, enabling high glass fiber contents (> 55%). It is known for final reinforced parts’ heat stability and high mechanical properties combi-ned with hydrolysis/glycolysis perfor-mances that are rated from high to even outstanding specifically in PPS. DS 8800 -11P also meets stringent requirements of food contact and drinkable water standards such as EC 10/2011, FDA, BfR and ACS.

3B Fiberglass CM6065 is a non-wo-ven mat made out of ECR glass _x005F_x001f_laments, consisting of continuous _x005F_x001f_bres randomly oriented in multiple layers. The glass _x005F_x001f_bre is bonded with a silane coupling agent and the layers held together with a suitable binder. The CM 6060 & CM 6065 family products contain an insoluble binder compatible with a large range of thermoset matrices like both un_x005F_x001f_lled or _x005F_x001f_lled unsaturated polyester (UP), vinyl ester (VE), epoxy (EP) Both CM 60606 and CM 6065 mats are characterized by their white color and are ideally suited for pultrusion pro-cesses for wide, long and heavy parts but as well for narrow and complex pro_x005F_x001f_les. The excellent mechanical properties provided by 3B CFM combined with the good electrical properties of the resins make the pultruded parts attractive for the electrical apparatus (high voltage), transportation industries and infrastruc-tures equipments.

3B Fiberglass 163D-14C chopped strand is specifically designed for excellent performances in injection and transfer molding processes & applications.The sizing coated at the glass fiber surface is engineered for enhanced compatibility with phenolic and epoxy resin systems.Thanks to its very light color, this product can be used in any natural grade compounds without impacting the color of the final part.Specific manufacturing technology provides 163D-14C chopped strand product with excellent dispersion and impregnation. As a result, this product offers excellent properties in a wide range of applications.

3B Fiberglass DS 1125-10N is designed to reinforce a broad range of polyamide resins, including PA6, PA66, PA610, PA6/66 copolymers and semi-aromatic PA.When molded this product exhibits outstanding dry mechanical properties and no sensitivity to mold release agents commonly used, such as calcium stearate. Its sizing has been designed in order to offer excellent dispersion properties. It can also reinforce and offer excellent performances in all flame retardant and impact modified polyamide formulations. Thanks to its very light color, this product can be used in any natural grade compounds without impacting the color of the final part. An innovative manufacturing techno-logy provides DS 1125-10N chopped strand with an excellent strand integrity and bulk density. As a result this product exhibits excellent feeding properties with very low fuzz generation.

3B Fiberglass 108F-14P is specifically designed to reinforce polycarbonate PC compounds with low glass fiber loading (5-15%).Its unique sizing technology results in exceptional performances in terms of dimensional stability, dispersion, mechanical properties and color. This product is not sensitive to flame retardant additives. 108F-14P is also very effective for the reinforcement of PVC resins. An innovative manufacturing technology provides 108F-14P with a very good strand integrity and bulk density. As a result, this product exhibits very good feeding properties with low fuzz generation compared to other glass fiber materials.

3B Fiberglass DS 7720-14P is designed to reinforce polyacetals POM resins with glass fiber. Its sizing has been developed specifically for POM and presents good properties in term of chemical and hydrolysis resistance. DS7720-14P has been developed in order to help reinforced plastics to meet the requirements of the most common food contact norms: EC 10/2011 and FDA Its very light color allows this product to be used in any natural grade compounds without impacting the color of the final part.An innovative manufacturing technology provides DS7720-14P chopped strand with an excellent bulk density. As a result, this product exhibits very good feeding properties compared to other competitive glass fiber materials.

3B Fiberglass CR 2080 consists of multiple continuous strands of smaller tex made from 3B E-CR glass wound onto a bobbin shape without mechanical twist and is free from static electricity generation.Choppable Roving CR2080 is silane sized and specifically designed for Sheet Molding Coumpound (SMC) application. SMC Rovings find appli-cations in automotive parts, sectional panel tanks, electrical items.2080 conforms to BS 14020 and IS 11320.

3B Fiberglass DS 3185E-10N is designed to reinforce polyester PBT resins. When molded this product exhibits excellent dry mechanical properties and good color characteristics.DS 3185E-10N can also reinforce and show excellent performances in blends with PET and flame-retardant formulations. An innovative manufacturing technology provides DS 3185E-10N chopped strand product with an excellent strand integrity and bulk density. As a result this product exhi-bits excellent feeding properties with low fuzz generation.DS 3185E-10N is also free of Nonylphenol Ethoxylates.

3B Fiberglass SE 2020 consist of conti-nuous filaments bonded into a single strand and wound onto a bobbin shape. A proprietary sizing applied on the fibers assures an excellent resin-to-glass bonding. SE 2020 Direct Rovings made of Advantex® glass are specifically designed for the production of Non Crimped Fabrics. The sizing of SE 2020 Direct Rovings is specifically designed for excellent adhesion with epoxy resin systems. SE 2020 Direct Rovings present high level of fatigue performances, supe-rior interfibre and interlaminar shear strengths. The SE 2020 Roving is approved by Germanischer Lloyd for the use in wind turbine rotor blades. SE 2020 Direct Rovings made of Advantex® glass can also be used in prepreg, filament winding processes.

3B Fiberglass 183F-11C is designed to reinforce PBT, ABS, ABS blends (with PC, PBT, PET) and styreni.When molded these products exhibit outstanding dry mechanical properties, and especially a high impact resistance. The versatile sizing gives also an excellent color in natural compounds and is suitable with flame retardant formulations. Specific manufacturing technology provides 183F-11C chopped strand product with excellent dispersibility. As a result, this product offers excellent properties in a wide range of applications.

3B Fiberglass W 3030 are specifically designed to provide significantly higher modulus, strength and enhanced fatigue performances versus traditional E-glass for wind tur-bine blades made out of unsaturated polyester, vinylester or Epoxy resin. HiPer-texTM W 3030 Rovings are per-fectly suited for the production of high modulus Non Crimped Glass Fabrics. The sizing W 3030 is purposely for-mulated for excellent adhesion with polyester, vinylester and Epoxy resin systems and leads to superior interfibre and interlaminar shear strengths as well as dynamic performances. The specific boron free glass formula-tion provides superior hydrolysis and corrosion resistance. These properties improvements versus typical E-glass will help blade desi-gners to push further the limits of glass fiber blade designs, especially for the long blades required for the multi MW turbines for on shore and off shore.

3B Fiberglass CM6060 is a non-wo-ven mat made out of ECR glass _x005F_x001f_laments, consisting of continuous _x005F_x001f_bres randomly oriented in multiple layers. The glass _x005F_x001f_bre is bonded with a silane coupling agent and the layers held together with a suitable binder. The CM 6060 & CM 6065 family products contain an insoluble binder compatible with a large range of thermoset matrices like both un_x005F_x001f_lled or _x005F_x001f_lled unsaturated polyester (UP), vinyl ester (VE), epoxy (EP) Both CM 60606 and CM 6065 mats are characterized by their white color and are ideally suited for pultrusion pro-cesses for wide, long and heavy parts but as well for narrow and complex pro_x005F_x001f_les. The excellent mechanical properties provided by 3B CFM combined with the good electrical properties of the resins make the pultruded parts attractive for the electrical apparatus (high voltage), transportation industries and infrastruc-tures equipments.

3B Fiberglass CR 3037 consists of multiple continuous strands of smaller tex made from 3B E-CR glass wound onto a bobbin shape without mechanical twist and is free from static electricity generation.Choppable Roving CR3037 is silane sized and specifically designed to produce single or multi-layer fabrics for automobile, boat building, che-mical tanks. CR3037 is also recom-mended for continuous filament wind application to manufacture pipes and tanks.3037 conforms to BS 14020 and IS 11320.

3B Fiberglass WS 6050 is designed to rein-force gypsum wallboards with glass fiber.Its sizing has been specifically deve-loped to enhance gypsum adhesion to glass fiber, to provide outstanding fiber dispersion and distribution in gypsum slurry and superior flowabi-lity of the fiber. As a result, this product exhibits very good feeding properties to deliver a dosing flow consistency, and to drastically improve fire resistance and mechanical properties of the gypsum boards.

3B Fiberglass DS 1128-10N is designed to reinforce a broad range of polyamide resins, including PA6, PA66, PA610, PA6/66 copolymers and semi-aromatic PA.When molded this product exhibits outstanding dry mechanical proper-ties, excellent hydrolysis/glycolysis resistance, high heat aging resis-tance and no sensitivity to mold release agents commonly used, such as calcium stearate. It can also reinforce and offer excellent perfor-mances in all impact modified and flame retardant polyamide formula-tions. An innovative manufacturing technology provides DS 1128-10N chopped strand with an excellent strand integrity and bulk density. As a result this product exhibits ex-cellent feeding properties with very low fuzz generation.The product is also designed for use in pneumatic conveying system and high throughput compounding line.

3B Fiberglass M8630 is a non-woven mat made out of ECR glass _x005F_x001e_laments, consisting of continuous _x005F_x001e_bres randomly oriented in multiple layers. The glass _x005F_x001e_bre is bonded with a silane coupling agent and the layers are held together with a suitable binder. The M8630 family products contain an insoluble binder compatible with a large range of thermoset matrices like both un_x005F_x001e_lled or _x005F_x001e_lled unsaturated polyester, vinyl ester, epoxy and polyurethane resin systems. The M8630 emulsion mat is ideally suited for matched metal die molding, RTM and S-RIM processes for molding _x005F_x001f_at, large and heavy panels or non complex parts. The excellent mechanical properties provided by 3B CFM combined with the good electri-cal properties of the resins make the molded parts attractive for applications like electrical apparatus (high voltage), transportation industries and infrastruc-tures equipments.

3B Fiberglass M8610 is a non-woven mat made out of ECR glass _x005F_x001f_laments, consisting of continuous _x005F_x001f_bres randomly oriented in multiple layers. The glass _x005F_x001f_bre is bonded with a silane cou-pling agent and the layers held together with a suitable binder.The CFM products contain an insolublebinder compatible with both un_x005F_x001f_lled or _x005F_x001f_lled unsaturated polyester, vinyl ester, epoxy and polyurethane resin systems. The M8610 mat is ideally suited for injection molding, RTM and S-RIM processes for molding complex parts. The M8615mat version, with its high rigidity, helps to work with large CFM cuts without loosing _x005F_x001f_bres. The excellent mechanical properties provided by CFM combined with the good electrical properties of the resins make the molded parts attractive for applications like electrical apparatus (high voltage), transportation & automo-tive industries and infrastructuresequipments.

3B Fiberglass 122Y-14P is designed to reinforce polycarbonate PC compounds and blends, where specific adhesion with the thermoplastic resin is required (glass fiber loading > 15%). The product also brings excellent reinforcement properties in polyphenylene oxide PPO or polyphelylene ether PPE resins.Due to its specific sizing chemistry, 122Y-14P offers an excellent compromise between high dry as molded performances and white color. It also has a very good compatibility with common flame retardant packages. An innovative manufacturing technology provides 122Y-14P with an excellent strand integrity and bulk density. As a result this product exhibits excellent feeding properties with very low fuzz generation.

3B Fiberglass DS 2200-10P is a 10 μm filament diameter, 4 mm long chopped glass fiber designed for production of high performance polyolefin compounds.DS 2200-10P shows outstanding compatibility with Polypropylene and enables improvements of material’s performances such as tensile and flexural strength, impact and creep, hence opening new design possibili-ties for lighter parts. DS 2200-10P is also designed for parts weathering in prolonged contact with water, deter-gents and glycol DS 2200-10P can also be used in applications complying with strin-gent requirements of food contact and drinkable water standards EC 10/2011, FDA, BfR and ACS. DS 2200-10P is supplied on a pel-letized form and offers outstanding feeding-to-extruder behavior as well as excellent fiber impregnation and dispersion.DS 2200-10P’s sizing chemistry also requires reduced amount of cou-pling agents to reach parts’ optimum mechanical performances.

3B Fiberglass M 8643 is a non-woven mat made out of E-CR glass filaments, consisting of continuous fibers randomly oriented in multiple layers. The glass fiber is bonded with a silane coupling agent and the layers held toge-ther with a suitable binder. The M 8643 products contain an inso-luble binder compatible with a large range of thermoset matrices like both unfilled or filled unsaturated polyester (UP), vinyl ester (VE), epoxy (EP) and polyurethane (PU) resin systems. The M 8643 emulsion mat is ideally suited for pultrusion processes for wide, long and heavy parts but also for narrow and complex profiles. The excellent mechanical properties provided by 3B CFM combined with the good electrical properties of the resins (i.e. UP) make the pultruded parts attractive for the electrical apparatus (high voltage), trans-portation industries and infrastructure equipments.

3B Fiberglass SE 1043 consists of continuous glass filaments bonded into a single strand and wound onto a bobbin shape without twist. A proprietary sizing applied on the fibers assures an excellent resin-to-glass bonding. Corrosion resistant SE 1043 Fibreglassmade of E-CR glass is specifi-cally designed for the manufacturing of composites pipes and under-ground & chemicals tanks. SE 1043 is also used in pultrusion to manufacture profiles and in weaving-knitting processes. SE 1043 is tested in compliance with BS 14020 and IS 11320.