To use, carefully align parts to be bonded, apply uniform pressure to maintain location. Follow curing guidelines given above. Timing should start once adhesive and substrate reach curing temperature.
- Application Method
- Syringe
Properties
- Typical Properties
- Uncured Properties
- Typical Cured Properties
| Value | Units | Test Method / Conditions | |
| Minimum Cure Temperature | 100 | °C | - |
| Chloride | max. 10 | ppm | - |
| Sodium Content | max. 10 | ppm | - |
| Potassium Content | max. 10 | ppm | - |
| Pot Life | 4 hours | - | - |
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity - HAT Viscometer (at 10 rpm at 25°C) | 20000 | cps | - |
| Specific Gravity | 1.19 | water 1 | - |
| Filler | Silver | - | - |
| Percent Silver (cured) | max. 5 | % | - |
| Theoretical Coverage (0.001" Wet Thickness) | 25 | in^2/gram | - |
| Solid Content | 71 | N/A | - |
| Value | Units | Test Method / Conditions | |
| Operating Temperature | -55 to +230 | °C | - |
| Peak Temperature | 325 | °C | - |
| Volume Resistivity (Z Axis) | 0.001 | Ω - cm | - |
| Volume Resistivity (X and Y Axis) | 1x10^12 | Ω - cm | - |
| Glass Transition Temperature | 100 | °C | - |
| Coefficient of Thermal Expansion | 50 | Ppm/°C | - |
| T-Shear Strength | 2100 | psi | - |
| Weight Loss (at 300°C, TGA) | 2.77 | % | - |
| Differential Scanning Calorimetry (DSC) Peak Tc | 168 | °C | - |
| Differential Scanning Calorimetry (DSC) ∆ Hc | -33.4 | J/g | - |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Test Data
Safety & Health
- Safety & Handling
- Use with adequate ventilation.
- Keep away from sparks and open flames.
- Avoid prolonged contact with skin and breathing of vapors.
- Wash with soap and water to remove from skin
Storage & Handling
- Shelf Life
- 1 year at ambient temperatures (Part A), 1 year at ambient temperatures (Part B)
- Curing Guidelines
These temperatures and times are presented as a guide only. The curing times are after substrate has been brought up to temperature. The end-user is encouraged to experiment to determine optimum curing schedule.
Temperature (°C) Time (sec.) 175 22-25 200 14 -18 210 4-6 - Handling And Storage
Prior to using, mix thoroughly to re-suspend fillers. If needed, 125-01A/B-187 can be thinned with small amounts of Creative Materials’ 102-03 thinner. Thinning should be done after mixing parts A and B to maintain proper mixing ratio.