Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Application Method
- B-stage Procedure
Apply adhesive to substrate. Next apply heat to advance the curing to the non-tacky stage (when cooled to room temperature). A temperature of 125°C for 2 - 3 minutes is required (B-Stage time is mass related). User is encouraged to experiment for optimum drying time at a given temperature. Store on release liner to prevent contamination.
- Bonding Procedure
Refer to above for storage information. To use, carefully align parts to be bonded, apply uniform pressure to maintain location. Cure for 30 minutes at 175°C, or 1 hour at 150°C. (Note cure times given are mass related. Timing should start after adhesive and substrates reach curing temperature.)
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Pot Life | Latent | — | — |
Conductivity | 6.6 | W/mK | — |
Viscosity | 20,000 - 35,000 | cps | — |
Thermal Conductivity | 6.6 | W/m-K | — |
Glass Transition Temperature | 105 | °C | — |
Lap Shear Strength | 1800 | psi | — |
Dielectric Strength | 440 | volts/mil | — |
Volume Resistivity | 1x10^16 | ohm-cm | — |
Dielectric Constant (at 1 Hz) | 5.2 | — | — |
Dielectric Factor (60 Hz) | 0.018 | — | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety & Handling
- Use with adequate ventilation.
- Keep away from sparks and open flames.
- Avoid prolonged contact with skin and breathing of vapors.
- Wash with soap and water to remove from skin.
Storage & Handling
- Shelf Life
- 2 month at 25ºC, 6 months at -10°C
- Suggested Handling & Curing
Material is ready to use as received. Store frozen to maintain consistent flow properties. Allow material to warm up to room temperature before opening container. Prior to using, mix container well to re-suspend fillers. As a coating cure for one (1) hour at 150°C, or 30 minutes at 175°C. 126-08 can be thinned with small amounts of CMI# 113-12 thinner.