Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
unfilled
longer processing time
high strength
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Mold probes for trimming of prototypes
Pattern plates
Foundry patterns
Core boxes
Control castings
Coping models
Negatives
Prototypes- Processing Instructions
The fillers should be stirred into the single components A and B, so they have nearly the same viscosity.
After the both components can be mixed very well. In case of small quantities and sufficient experience it is also possible to mix the unfilled components first and then to stir into the filler, without making the potlife too short for casting.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Flexural strength | 40 ± 3 | MPa | EN ISO 178 |
Viscosity (25°C) | 50 - 100 | mPa.s | — |
Density (20°C) | 1,10 ± 0,02 | g/cm3 | — |
Pot Life (200g/20°C) | 5-7 | minutes | — |
Curing time at RT | 0,5 - 1,5 | Hrs | — |
Flexural Strength | 40 ± 3 | MPa | EN ISO 178 |
Flexural Elongation at Break | 7,6 ± 0,3 | % | EN ISO 178 |
Flexural Modulus | 1000 ± 100 | MPa | EN ISO 178 |
Impact Resistance (Charpy) | 20 ± 4 | kJ/m2 | EN ISO 179 |
Compressive Strength | 34 ± 3 | MPa | EN ISO 604 |
Shore Hardness | 67 ± 2 | Shore D | DIN ISO 7619-1 |
Packaging & Availability
- Packages
1,000 kg / 5,000 kg / 50,000 kg
Storage & Handling
- Storing
Storage at room temperature 18-25 °C.
Opened containers should be closed immediately after use and should be used up as soon as possible.