The fillers should be stirred into the single components A and B, so that they have nearly the same viscosity.
After that both components can be very well mixed. In case of small quantities and sufficient experience it is also possible to mix the unfilled components first and then to stir in the filler, without making the potlife too short for casting.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Shore hardness | 67 ± 2 | Shore A | DIN ISO 7619-1 |
Compressive Strength | 34 ± 3 | MPa | EN ISO 604 |
Viscosity (25°C) | 200 ± 80 | mPa.s | — |
Compressive Strength | 32 ± 5 | MPa | EN ISO 604 |
Flexural elongation at break | 7.6 ± 0.3 | % | EN ISO 178 |
Density (20°C) | 1,06 ± 0,02 | g/cm3 | — |
Flexural modulus | 1000 ± 100 | MPa | EN ISO 178 |
Pot Life (200g/20°C) | 9-15 | minutes | — |
Impact resistance (Charpy) | 20 ± 4 | kJ/m2 | EN ISO 179 |
Curing time at RT | 5-8 | Hrs | — |
Flexural Strength | 38 ± 5 | MPa | EN ISO 178 |
Flexural Elongation at Break | 7,6 ± 0,3 | % | EN ISO 178 |
Flexural Modulus | 1025 ± 150 | MPa | EN ISO 178 |
Impact Resistance (Charpy) | 30 ± 5 | kJ/m2 | EN ISO 179 |
Heat Resistance (HDT) | 69 ± 2 | °C | DIN EN ISO 75 B |
Shore Hardness | 72 ± 2 | Shore D | DIN ISO 7619-1 |
Packaging & Availability
- Packages
1,000 kg / 5,000 kg / 50,000 kg
Storage & Handling
- Storing
Storage at room temperature 18-25 °C.
Opened containers should be closed immediately after use and should be used up as soon as possible.