Products

WIPELAST TV 30 BK UV is a black polypropylene-EPDM composite material with 30% talc filler and UV stabilizers, specifically designed for use in the automotive industry. Prior to processing, the material must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to achieve a maximum moisture content of 0.10%. During processing, the melt temperature should be maintained at 200-270°C, with a mold temperature of 20-60°C during injection molding.

WIPAFLEX TV 10 BK UV is a black composite material suitable for various automotive market segments. It contains polypropylene-polyethylene-EPDM as the base polymer and 10% talc filler. To achieve optimal processing conditions, it must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to ensure a maximum moisture content of 0.10%. The recommended processing method is injection molding, with a melt temperature range of 200-270°C and a mold temperature range of 20-60°C.

WIPAFLEX TV 5 BK is a black composite material suitable for various automotive market segments. It contains polypropylene-polyethylene-EPDM as the base polymer and 5% talc filler. To achieve optimal processing conditions, it must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to ensure a maximum moisture content of 0.10%. The recommended processing method is injection molding, with a melt temperature range of 200-270°C and a mold temperature range of 20-60°C.

WIPELAST TV 10 BK UV is a black composite material suitable for various automotive market segments. It consists of polypropylene-EPDM as the base polymer and 10% talc filler. The material is UV stabilized, which is its special feature. To achieve optimal processing conditions, it must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to ensure a maximum moisture content of 0.10%. The material is recommended for processing using injection molding, with a melt temperature of 200-270°C and a mold temperature of 20-60°C.

WIPAFLEX TV 10 BK is a black material with heat-age stabilization properties intended for use in various automotive applications. The material is a blend of polypropylene, polyethylene, and EPDM, with 10% talc added as a filler. Prior to processing via injection molding, the material must be pre-dried at temperatures between 60 and 100°C for 2-4 hours, depending on its moisture content, which should not exceed 0.10%. During injection molding, the material should be melted at temperatures ranging from 200 to 270°C, with a mold temperature between 20 and 60°C. All temperatures must be carefully monitored to ensure they fall within the specified ranges.

WIPELAST TV 30 BK is a black composite made of polypropylene-EPDM, containing 30% talc filler. It is suitable for a variety of markets, including the automotive industry. Pre-drying is necessary at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to achieve a maximum moisture content of 0.10%. Injection molding is recommended, with a melt temperature of 200-270°C and a mold temperature of 20-60°C.

WIPELAST TV 10 BK is a black composite material suitable for various automotive market segments. It contains polypropylene-EPDM as the base polymer and 10% talc filler. To achieve optimal processing conditions, it must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to ensure a maximum moisture content of 0.10%. The recommended processing method is injection molding, with a melt temperature range of 200-270°C and a mold temperature range of 20-60°C.

WIPELAST TV 20 BK is a black composite material suitable for use in the automotive market segment. It consists of polypropylene-EPDM as the base polymer and 20% talc filler. To achieve optimal processing conditions, it must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to ensure a maximum moisture content of 0.10%. The material is recommended for processing using injection molding, with a melt temperature of 200-270°C and a mold temperature of 20-60°C.

WIPELAST TV 20 BK UV is a black composite material with a base of polypropylene-EPDM and 20% talc filler, specifically designed for use in the automotive market segment. It has been UV-stabilized to enhance its performance under UV exposure. To achieve optimal processing conditions, the material must be pre-dried at 60-100°C in an air-circulating dryer for 2-4 hours, depending on the initial moisture content, to ensure a maximum moisture content of 0.10%.