LNP™ LUBRICOMP™ Compound RL003

Identification & Functionality

Additives Included

Heat Stabilizer,

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

PTFE

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Friction Resistant,

Good Mold Release,

Heat Stabilized,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Rail & Mass Transit

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Electronic Components,

Engine Component,

Helical Gear,

Home Appliances,

Interior Rail Components,

Personal Accessories,

Pinion,

Pool Covers,

Sporting Goods,

Spur Gear,

Tablets,

Tarpaulins,

Turf Applications,

Windows,

Wireless Communication

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	59	MPa	ISO 527
Tensile Stress (Break) ¹¹	73	MPa	ASTM D638
Tensile Stress (Break) ¹¹	73	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	7	%	ISO 527
Tensile Strain (Break) ¹¹	11	%	ASTM D638
Tensile Strain (Break) ¹¹	8.9	%	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	83	MPa	ISO 178
Flexural Stress ¹¹	103	MPa	ASTM D790
Flexural Stress ¹¹	90	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2300	MPa	ISO 178
Flexural Modulus ¹¹	2900	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.23	g/cm³	ISO 1183
Density ¹¹	1.23	g/cm³	ASTM D792
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1 - 3	%	ISO 294
Wear Factor Washer ¹¹	28	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.32	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.3	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000111	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000115	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	82	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	45	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, at 23°C) ¹¹	1014	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	32	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	275 - 290	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 