LNP THERMOCOMP™ Compound - D251RCC - SABIC's Specialty

Identification & Functionality

Additives Included: Flame Retardant,
Heat Stabilizer,
Mold Release Agent
Chemical Family: Polycarbonate (PC)
Fillers Included: Glass Fiber,
Silicone Oil
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Basic Thermoplastics
Recycled Polymers
Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Labeling Claims: Bromine-free,
Chlorine-free,
Contains PCR Resin,
Recyclable,
Recycled,
Sustainable
Materials Features: Cost Effective,
Flame Retardant,
Good Aesthetics,
Good Mold Release,
Heat Stabilized,
High Ductility,
High Impact Resistance,
High Modulus,
High Stiffness,
Low Warpage,
Non-Halogenated,
Non-brominated,
Non-chlorinated,
Recyclable,
UL Listed
Mechanical Recycling: Process

Debris are washed, melted & transformed into raw material for a new process. Focus on responsible sourcing of high-quality waste streams

Certification

Third-party certification of PCR content conducted by SCS Global Services

Value Proposition

21-80% post-consumer recycled content

Meeting RoHS1 guidelines

Provides CO2

reduction & waste depletion options

Non-brominated & non-chlorinated flame retardant systems

Up to 2 extra EPEAT points can be achieved

Broad color space, enhanced performance via

blending with copolymers

Drop in solution to existing tools

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Housings & Enclosures,
Switches & Relays
Plastics & Elastomers End Uses: Building Materials,
Cell Phones,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical Housing,
Electrical/Electronic Applications,
Electronic Components,
Garden Equipment,
Laptop Housing,
Lawn Equipment,
Mobile Phone Housings,
PC Housing,
Personal Accessories,
Pool Covers,
Tablet Housing,
Tablets,
Tarpaulins,
Turf Applications,
Wearable Device Housing,
Windows
Plastics & Elastomers Processing Methods: Injection Molding
Potential Applications: PC based LNP THERMOCOMP™ compounds may be qualified to use in consumer electronics, industrial applications for combination of dimensional stability, thin wall and non-Br/Cl Eco FR systems.

Properties

Flame Rating: UL 94 V0
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

	Value	Units	Test Method / Conditions
Tensile Modulus (at 5 mm/min) ¹¹	6650	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	100	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.9	%	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	6300	MPa	ASTM D790
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	161	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	6750	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	108	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.1	%	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	6100	MPa	ISO 178
Flexural Strength (at 2 mm/min) ¹¹	157	MPa	ISO 178

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	114	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	119	°C	ASTM D648
Vicat Softening Temperature (Rate B/50) ¹¹	122	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	125	°C	ISO 306
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.000025	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.000074	1/°C	ASTM E831

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	139	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	94	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	616	J/m	ASTM D4812
Izod Impact (Notched, 80104, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	9	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	38	kJ/m²	ISO 180/1U
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	24	J	ASTM D3763

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 0.6	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ THERMOCOMP™ Compound D251RCC