Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
| Value | Units | Test Method / Conditions | |
| Hardness (Rockwell M) | 109 | — | ASTM D785 |
| Tensile Stress (Yield, Type I, 5 mm/min) | 110 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) | 7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) | 60 | % | ASTM D638 |
| Tensile Stress (Yield, 50 mm/min) | 105 | MPa | ISO 527 |
| Ball Indentation Hardness (H358/30) | 140 | MPa | ISO 2039-1 |
| Tensile Modulus (at 5 mm/min) | 3580 | MPa | ASTM D638 |
| Tensile Strain (Yield, 50 mm/min) | 6 | % | ISO 527 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) | 151 | MPa | ASTM D790 |
| Tensile Strain (Break, 50 mm/min) | 60 | % | ISO 527 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) | 3300 | MPa | ASTM D790 |
| Tensile Modulus (at 1 mm/min) | 3200 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) | 160 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) | 3300 | MPa | ISO 178 |
| Taber Abrasion (CS-17, 1 kg) | 10 | mg/1000cy | ASTM D1044 |
| Value | Units | Test Method / Conditions | |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Bulk Density | 0.78 | g/cm³ | ASTM D1895 |
| Bulk Density | 780 | kg/m³ | ISO 1183 |
| Mean Resin Particle Size | 15 | micrometer | SABIC method |
| Poisson's Ratio | 0.36 | — | ASTM E132 |
| Specific Gravity | 1.27 | — | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) | 0.5 - 0.7 | % | SABIC method |
| Water Absorption (at 23°C, 24hrs) | 0.25 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) | 1.25 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) | 1.25 | % | ISO 62-1 |
| Mold Shrinkage (flow, 3.2 mm) | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 337°C, 6.6 kgf) | 9 | g/10 min | ASTM D1238 |
| Moisture Absorption (at 23°C, 50% RH) | 0.7 | % | ISO 62 |
| Melt Volume Rate (at 360°C, 5.0 kg) | 13 | cm³/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (Rate B/50) | 211 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) | 218 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) | 210 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 150°C, flow) | 5.00E-05 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) | 201 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -20°C to 150°C, flow) | 0.0000558 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 150°C, xflow) | 0.00005 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -20°C to 150°C, xflow) | 0.000054 | 1/°C | ASTM E831 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) | 200 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) | 190 | °C | ISO 75/Ae |
| Thermal Conductivity | 0.22 | W/m-°C | ASTM C177 |
| Thermal Conductivity | 0.24 | W/m-°C | ISO 8302 |
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (1 MHz) | 2.9 | — | IEC 60250 |
| Relative Permittivity (1 kHz) | 3.15 | — | ASTM D150 |
| Relative Permittivity (50/60 Hz) | 2.9 | — | IEC 60250 |
| Volume Resistivity | 1.00E+15 | Ω.cm | IEC 60093 |
| Volume Resistivity | 1.00E+17 | Ω.cm | ASTM D257 |
| Dielectric Strength (in air, at 1.6mm) | 32.7 | kV/mm | ASTM D149 |
| Dielectric Strength (in oil, at 0.8mm) | 33 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) | 25 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) | 28 | kV/mm | ASTM D149 |
| Dielectric Strength (in oil, at 3.2mm) | 16 | kV/mm | IEC 60243-1 |
| Dissipation Factor (at at 1 kHz) | 0.0013 | — | ASTM D150 |
| Dissipation Factor (at 2450 MHz) | 0.0025 | — | ASTM D150 |
| Dissipation Factor (at 2450 MHz) | 0.0025 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) | 0.0005 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) | 0.006 | — | IEC 60250 |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Unnotched, at 23°C) | 1335 | J/m | ASTM D4812 |
| Color (at 23°C) | 36 | J | ASTM D3029 |
| Izod Impact (Notched, at 23°C) | 53 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) | 6 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Back Pressure | 0.3 - 0.7 | MPa | — |
| Drying Temperature | 150 | °C | — |
| Drying Time | 4 - 6 | Hrs | — |
| Drying Time (Cumulative) | 24 | Hrs | — |
| Front - Zone 3 Temperature | 345 - 400 | °C | — |
| Maximum Moisture Content | 0.02 | % | — |
| Melt Temperature | 350 - 400 | °C | — |
| Middle - Zone 2 Temperature | 340 - 400 | °C | — |
| Mold Temperature | 135 - 165 | °C | — |
| Nozzle Temperature | 345 - 400 | °C | — |
| Rear - Zone 1 Temperature | 330 - 400 | °C | — |
| Screw Speed | 40 - 70 | rpm | — |
| Shot to Cylinder Size | 40 - 60 | % | — |
| Vent Depth | 0.025 - 0.076 | mm | — |
| Value | Units | Test Method / Conditions | |
| Oxygen Index (LOI) | 47 | % | ASTM D2863 |
| Oxygen Index (LOI) | 47 | % | ISO 4589 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability