Low smoke, low-toxicity, halogen-free, flame-retardant thermoplastic black compound for use in all types of cables sheathing. This compound presents a high flame retardancy, which allow cables to comply with harder flame tests and high CPR classifications (depending always on cable construction)
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Appearance
- Pellets
- Mechanical Properties
- Physical Properties
- Electrical Properties
- Fire & Smoke Properties
- Thermo-Mechanical Properties
Value | Units | Test Method / Conditions | |
Elongation at Break | 170 | % | IEC 60811-501 |
Elongation at Break (After Thermal Aging: 7 Days at 100ºC) | -12 | % Variation | IEC 60811-401 |
Tensile Strength (at Break) | 13 | N/mm² | IEC 60811-501 |
Tensile Strength (After Thermal Aging: 7 Days at 100ºC) | 12 | % Variation | IEC 60811-401 |
Value | Units | Test Method / Conditions | |
Density | 1.54 | g/cm³ | BS EN ISO 1183-3 |
Melt Flow Rate (at 150°C / 21.6 kg) | 7 | g/10 min | Internal Method |
Tear Strength | 6 | N/mm | BS 6469-99.1 |
Value | Units | Test Method / Conditions | |
Insulation Constant Ki Resistance (at 20ºC) | 7.7 | MOhm/km | EN 50395 |
Insulation Constant Ki Resistance (at 90ºC) | 0.057 | MOhm/km | EN 50395 |
Value | Units | Test Method / Conditions | |
Halogen Acid Gas Evolution | max. 0.5 | % | IEC 60754-1 |
Temperature Index | min. 300 | °C | BS ISO 4589-3 |
Temperature Index | min. 572 | °F | BS ISO 4589-3 |
Limiting Oxygen Index | 41 | % | BS ISO 4589-2 |
Value | Units | Test Method / Conditions | |
Cold Bend (at -30°C) | Pass | No Cracks | IEC 60811-504 |
Elongation at Break: (at -30°C) | 50 (Pass) | % | IEC 60811-505 |
Hot Pressure Deformation (at 90°C) | 35 | % | IEC 60811-508 |
Technical Details & Test Data
- Processing
Extruder - An extruder with an L/D ratio (length/diameter) between 15 and 24 and a screw with a compression ratio 1.2:1 are recommended.
Extruder Temperature Conditions - It is important that the melt temperature is not allowed to increase above 160°C. As a guide the following temperature profile is recommended:Zone #1 Zone #1 Zone #1 Zone #1 Head Die Celsius 130°C 140°C 145°C 150°C 160°C 160°C Fahrenheit 266°F 284°F 293°F 302°F 320°F 320°F This profile will vary slightly depending on extruder type, head design and output
Screw Water Temperature - Not mandatory, if present we recommend 40°-60°C
Recommended Screen Pack - Spacer ring or breaker plate only
Head & Tool Design: The head and tools should be so designed as to allow streamlined flow of material. To obtain the optimum in physical properties in the case of tubing tools, a maximum draw down ratio of 1.5:1 is recommended to avoid internal stresses.Color Masterbatches: EVA, preferable, and PE based color masterbatches including black, up to a maximum of 1%, have no detrimental effect on the properties. It is recommended that all masterbatches should be thoroughly dried before use for 8 hours at 60°C or 4 hours at 80°C in a de-humidifying drier.
Packaging & Availability
- Packaging
the following possibilities are available:
- Moisture resistant sacks containing 25kg
- Boxes with a moisture resistant heat sealed liner containing approximately 600kg
Storage & Handling
- Storage & Shelf Life
This material has unlimited shelf life. The following storage conditions are recommended:
- Packaging should remain sealed
- Avoid storage outside and in direct sunlight.