Features & Benefits
- Materials Features
- Properties
high heat resistance
excellent flow properties
medium E-modulus
good impact strength
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Functional parts automotive field
Functional parts EDP field
Prototyping parts EDP field
Prototypes in the automotive field
Cladding parts automotive field
Cladding parts EDP field- Processing Instructions
Processing instructions
It is essential to stir component A before use, as the additives tend to sedimentation. Component B has not to be stirred.
The molding tools should be made of a polyurethane- resp. epoxy resin system, with a high-quality surface.
In order to improve the surface appearance of the component, it is possible (but no must to do!):- to preheat the material to 30 °C
- to preheat the molds to 40 - 50 °C
A combination of preheated material and molds is the optimum.
The wall thicknesses of the components are approx. 5 mm. Ribs or bigger material accumulations can also be produced.
Shrinkage of the parts depends on geometry, wall thickness and temperature. Laboratory values are available on demand.
The components can be demoulded after approx. 10 min. This can differ accordingly to wall thickness and temperature.
The postcuring has to be made by means of a supporting structure.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Shore hardness | 80 ± 3 | Shore D | DIN ISO 7619-1 |
| Density (20°C) | 1,19 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 7.4 ± 0.2 | % | EN ISO 178 |
| Pot Life (20°C) | 55 - 60 | minutes | — |
| Flexural modulus | 1640 ± 50 | MPa | EN ISO 178 |
| Curing time at RT | 10-15 | Hrs | — |
| Flexural strength | 65 ± 1 | MPa | EN ISO 178 |
| Post Curing | 4 (120) | Time in h (Temperature in °C) | — |
| Glass transition temperature TG | 124 ± 5 | °C | — |
| Heat resistance (HDT) | 102 ± 5 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 38 ± 8 | kJ/m2 | EN ISO 179 |
Packaging & Availability
- Packages
Comp. A MG 804 Comp. A (polyol) 1,000 kg / 5,000 kg Comp. B MG 804 Comp. B (isocyanate) 1,000 kg / 5,000 kg
Storage & Handling
- Storing
Storage at room temperature 18-25 °C.
Opened containers should be closed immediately after use and should be used up as soon as possible.