LNP LUBRICOMP™ Compound - DL003 - SABIC's Specialty - PC

Identification & Functionality

Additives Included: Lubricant (PTFE)
Chemical Family: Polycarbonate (PC)
Fillers Included: PTFE
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Consumer Goods,
Electrical & Electronics,
Healthcare & Pharma,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Aftermarket Parts & Components
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Healthcare & Pharma — Medical
Medical Devices & Assemblies
Printing & Packaging — Packaging
Healthcare Packaging,
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Housings & Enclosures,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Electronic Components,
Enclosure,
Energy Management,
Home Appliances,
Medical Devices,
Modular Panel,
Personal Accessories,
Pharmaceutical Packaging,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications,
Weaving Machine,
Windows,
Wireless Communication
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 HB,
UL 94 V1
Physical Properties
Mechanical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

	Value	Units	Test Method / Conditions
Density ¹¹	1.28	g/cm³	ISO 1183
Density ¹¹	1.28	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.05 - 0.2	%	ASTM D570
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	6.2	g/10 min	ASTM D1238
Water Absorption (at 23°C, 24hrs) ¹¹	0.2 - 0.3	%	ASTM D570
Water Absorption (at 23°C, 24hrs) ¹¹	0.2 - 0.3	%	ISO 62-1
Wear Factor Washer ¹¹	60	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.18	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.26	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.05 - 0.2	%	ISO 62
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	5.8	cm³/10 min	ISO 1133
Mold Shrinkage (flow) ᵍ ¹¹	0.7 - 0.9	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.7 - 0.9	%	SABIC method

	Value	Units	Test Method / Conditions
Tensile Modulus (at 50 mm/min) ¹¹	2150	MPa	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	37.6	%	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	6.1	%	ASTM D638
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	51	MPa	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2190	MPa	ASTM D790
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	82	MPa	ASTM D790
Flexural Modulus (at 2 mm/min) ¹¹	2100	MPa	ISO 178
Flexural Strength (at 2 mm/min) ¹¹	81	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	2200	MPa	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	20	%	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	5.1	%	ISO 527
Tensile Stress (Yield, 50 mm/min) ¹¹	54	MPa	ISO 527

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	127	°C	ASTM D648
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000076	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000098	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	128	°C	ISO 75/Af
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	138	°C	ISO 75/Bf
Vicat Softening Temperature (Rate B/50) ¹¹	144	°C	ASTM D1525
Vicat Softening Temperature (Rate B/50) ¹¹	144	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	144	°C	ISO 306

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	280	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	30	J	ASTM D3763
Izod Impact (Notched, 80104, at 23°C) ¹¹	20	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	140	kJ/m²	ISO 180/1U
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	22	kJ/m²	ISO 179/1eA
Charpy Impact (at 23°C, Unnotch Edgew 80104 sp=62mm) ¹¹	180	kJ/m²	ISO 179/1eU
Multi-Axial Impact ¹¹	34	J	ISO 6603

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 1.5	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ᵖ	min. 3	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ LUBRICOMP™ Compound DL003