LNP™ THERMOCOMP™ Compound DF0081PI

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer,

Impact Modifier,

Metal Deactivator,

Mold Release Agent

Chemical Family

Polycarbonate (PC)

Fillers Included

Glass Fiber,

Talc

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free

Materials Features

Cost Effective,

Flame Retardant,

Good Mold Release,

Heat Stabilized,

High Ductility,

High Impact Resistance,

High Modulus,

High Stiffness,

Impact Modified,

Low Warpage,

Non-brominated,

Non-chlorinated

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Lighting

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Building Materials,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Garden Equipment,

LED Lighting,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Tablets,

Tarpaulins,

Turf Applications,

Windows,

Wireless Communication

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0,

UL 94 V1,

UL 94 V2

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	130	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	12700	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	170	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	10000	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	123	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	12500	MPa	ISO 527
Flexural Strain (Break, at 2 mm/min) ¹¹	1.9	%	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	10800	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.54	g/cm³	ASTM D792
Mold Shrinkage (flow) ᵍ ¹¹	0.4	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.41	%	SABIC method

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	110	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	102	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	264	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	81	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	10	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	22	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	9	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	110	°C	—
Drying Time ⁷	3 - 6	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	285 - 310	°C	—
Nozzle Temperature ⁷	285 - 305	°C	—
Front - Zone 3 Temperature ⁷	280 - 300	°C	—
Middle - Zone 2 Temperature ⁷	270 - 290	°C	—
Rear - Zone 1 Temperature ⁷	260 - 280	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.1 - 0.3	MPa	—
Screw Speed ⁷	50 - 90	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 1.2	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ᵖ	min. 1	mm	UL 94
UL Recognized (94V-2 Flame Class Rating) ᵖ	min. 0.5	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America