Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.23 | — | ASTM D792 |
Specific Gravity ¹¹ | 1.25 | — | ASTM D792 |
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
Density ¹¹ | 1.25 | g/cm³ | ISO 1183 |
Water Absorption (at 23°C, saturated) ¹¹ | 0.22 | % | ISO 62-1 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.07 | % | ISO 62 |
Melt Volume Rate (at 280°C, 10.0 kg) ¹¹ | 12 | cm³/10 min | ISO 1133 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.5 | % | SABIC method |
Value | Units | Test Method / Conditions | |
Taber Abrasion (CS-17, 1 kg) ¹¹ | 65 | mg/1000cy | SABIC method |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 106 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5 | % | ASTM D638 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 80 | MPa | ISO 527 |
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 151 | MPa | ASTM D790 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 5720 | MPa | ASTM D790 |
Tensile Modulus (at 1 mm/min) ¹¹ | 5500 | MPa | ISO 527 |
Flexural Stress (Break, 2 mm/min) ¹¹ | 125 | MPa | ISO 178 |
Hardness (Rockwell L) ¹¹ | 106 | — | ASTM D785 |
Flexural Modulus (at 2 mm/min) ¹¹ | 4500 | MPa | ISO 178 |
Ball Indentation Hardness (H358/30) ¹¹ | 125 | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00005 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00005 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ISO 11359-2 |
Thermal Conductivity ¹¹ | 0.28 | W/m-°C | ISO 8302 |
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00003 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
Ball Pressure Test (approximate maximum) ¹¹ | 135 | °C | IEC 60695-10-2 |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 132 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.000036 | 1/°C | ASTM E831 |
Vicat Softening Temperature (Rate A/50) ¹¹ | 150 | °C | ISO 306 |
Relative Temperature Index (Electrical) ¹¹ | 110 | °C | UL 746B |
Vicat Softening Temperature (Rate B/50) ¹¹ | 140 | °C | ISO 306 |
Relative Temperature Index (Mechanical with impact) ¹¹ | 105 | °C | UL 746B |
Vicat Softening Temperature (Rate B/120) ¹¹ | 145 | °C | ISO 306 |
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 135 | °C | ISO 75/Be |
Relative Temperature Index (Mechanical without impact) ¹¹ | 110 | °C | UL 746B |
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 130 | °C | ISO 75/Ae |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
Dielectric Strength (in oil, at 0.8mm) ¹¹ | 30 | kV/mm | IEC 60243-1 |
Dielectric Strength (in oil, at 1.6mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
Dielectric Strength (in oil, at 3.2mm) ¹¹ | 16 | kV/mm | IEC 60243-1 |
Dielectric Strength (in oil, at 3.2mm) ¹¹ | 23.6 | kV/mm | ASTM D149 |
Relative Permittivity (1 MHz) ¹¹ | 2.9 | — | IEC 60250 |
Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0016 | — | ASTM D150 |
Dissipation Factor (at 50/60 Hz) ¹¹ | 0.004 | — | IEC 60250 |
Dissipation Factor (at at 1 MHz) ¹¹ | 0.002 | — | IEC 60250 |
Comparative Tracking Index ʳ ¹¹ | 225 | V | IEC 60112 |
Relative Permittivity (50/60 Hz) ¹¹ | 3 | — | IEC 60250 |
Relative Permittivity (50/60 Hz) ¹¹ | 2.98 | — | ASTM D150 |
Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
Comparative Tracking Index (UL, PLC) ¹¹ | 1 | PLC Code | UL 746A |
High Ampere Arc Ignition (PLC 3) ¹¹ | min. 6 | mm | UL 746A |
High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
High Ampere Arc Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
Arc Resistance (Tungsten, PLC) ¹¹ | 7 | PLC Code | ASTM D495 |
Hot Wire Ignition (PLC) ¹¹ | 0 | PLC Code | UL 746A |
High Ampere Arc Ignition (Surface, PLC) ¹¹ | 1 | PLC Code | UL 746A |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
Izod Impact (Notched, at 23°C) ¹¹ | 106 | J/m | ASTM D256 |
Izod Impact (Notched, at -40°C) ¹¹ | 96 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 100 - 120 | °C | — |
Drying Temperature ⁷ | 110 - 120 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time ⁷ | 2 - 3 | Hrs | — |
Melt Temperature ⁷ | 280 - 300 | °C | — |
Melt Temperature ⁷ | 300 - 325 | °C | — |
Nozzle Temperature ⁷ | 260 - 280 | °C | — |
Nozzle Temperature ⁷ | 300 - 325 | °C | — |
Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
Front - Zone 3 Temperature ⁷ | 290 - 325 | °C | — |
Middle - Zone 2 Temperature ⁷ | 260 - 280 | °C | — |
Middle - Zone 2 Temperature ⁷ | 275 - 320 | °C | — |
Rear - Zone 1 Temperature ⁷ | 240 - 260 | °C | — |
Rear - Zone 1 Temperature ⁷ | 265 - 315 | °C | — |
Hopper Temperature ⁷ | 60 - 80 | °C | — |
Mold Temperature ⁷ | 80 - 110 | °C | — |
Mold Temperature ⁷ | 80 - 120 | °C | — |
Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 20 - 100 | rpm | — |
Screw Speed ⁷ | 20 - 1000 | rpm | — |
Shot to Cylinder Size ⁷ | 30 - 70 | % | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2 | mm | UL 94 |
UL Recognized (94V-0 Flame Class Rating) ʳ | min. 6 | mm | UL 94 |
UL Recognized (94V-0 Flame Class Rating) ʳ | 5.99 | mm | UL 94 |
UL Recognized (94V-0 Flame Class Rating) ʳ | 6 | mm | UL 94 |
UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
UL Recognized (94V-1 Flame Class Rating) ʳ | 1.5 | mm | UL 94 |
UL Recognized (94V-1 Flame Class Rating) ʳ | 1.47E+00 | mm | UL 94 |
Glow Wire Flammability Index (at 1 mm) ʳ | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
UV-light (Water exposure/immersion) ʳ | F2 | — | UL 746C |
Oxygen Index (LOI) ʳ | 30 | % | ISO 4589 |
Oxygen Index (LOI) ʳ | 27 | % | ASTM D2863 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability