NORYL™ Resin SE1GFN2

Identification & Functionality

Additives Included

Flame Retardant

Fillers Included

Glass Fiber

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free

Materials Features

Amorphous,

Dimensional Stability,

Flame Retardant,

Good Stiffness,

High Hydrolytic Stability,

High Stiffness,

Low Moisture Absorption,

Low Shrinkage,

Low Specific Gravity,

Low Warpage,

Non-Halogenated,

Non-brominated,

Non-chlorinated

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Healthcare & Pharma,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Aftermarket Parts & Components,

Electrical & Electronic Systems

Building & Construction — Building Materials

Interior Fixtures,

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Automotive Electronics,

Consumer Electronics,

Displays,

Lighting

Consumer Goods — Luggage & Leather Goods

Healthcare & Pharma — Medical

Laboratory & Diagnostics,

Medical Devices & Assemblies

Industrial — Military & Defense

Advanced Materials

Electrical & Electronics — Parts & Components

Batteries,

Connectors,

Housings & Enclosures,

Sensors & Actuators,

Switches & Relays,

Terminal Blocks, Plugs & Sockets

Industrial — Power, Water & Utilities

Renewable Energy

Plastics & Elastomers End Uses

AC Charging Cabinet,

Air Conditioner,

Audio Equipment,

Automotive Under The Hood,

Batteries,

Battery Pack,

Battery Protection,

Building Materials,

Cash Dispenser (ATM),

Cell Phones,

Circuit Protection,

Clinical Diagnostics,

Computer Components,

Connectors,

Covers,

Defense Vehicles,

Dishwasher,

Displays,

Drain Pan,

EV Battery,

Electric Vehicles,

Electrical Components,

Electrical Housing,

Electrical/Electronic Applications,

Electronic Components,

Enclosure,

Energy Management,

Fittings,

Fixture Bath/Shower,

Fuse Box,

HVAC,

Heavy Vehicles,

Hot Water System,

Housings,

Ignition System,

Inverters,

Junction Boxes,

Kitchen & Coffee Machines,

Labware,

Micro Inverter,

Microwave Oven,

Motorcycle,

Non-LED Lighting,

Photovoltaic Device,

Pipes,

Power Manangement,

Pumps,

Sensor,

Sockets,

Solar Panels,

Suitcase,

Surgical Devices,

Switches,

Tablets,

Ticket Machine,

Washing Machine,

Wearable Device,

Wireless Communication,

Wiring Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 5VA,

UL 94 V0,

UL 94 V1

Mechanical Properties

	Value	Units	Test Method / Conditions
Taber Abrasion (CS-17, 1 kg) ¹¹	65	mg/1000cy	SABIC method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	106	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	120	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	3	%	ASTM D638
Tensile Stress (Break, 5 mm/min) ¹¹	80	MPa	ISO 527
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹	151	MPa	ASTM D790
Tensile Modulus (at 5 mm/min) ¹¹	7100	MPa	ASTM D638
Tensile Strain (Break, 5 mm/min) ¹¹	2	%	ISO 527
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹	5720	MPa	ASTM D790
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	140	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	6400	MPa	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	5500	MPa	ISO 527
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	5500	MPa	ASTM D790
Flexural Stress (Break, 2 mm/min) ¹¹	125	MPa	ISO 178
Hardness (Rockwell L) ¹¹	106	—	ASTM D785
Flexural Modulus (at 2 mm/min) ¹¹	5600	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4500	MPa	ISO 178
Tensile Stress (Break, 50 mm/min) ¹¹	100	MPa	ISO 527
Ball Indentation Hardness (H358/30) ¹¹	125	MPa	ISO 2039-1
Tensile Strain (Break, 50 mm/min) ¹¹	2.5	%	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	150	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.23	—	ASTM D792
Specific Gravity ¹¹	1.25	—	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.11	%	ISO 62-1
Water Absorption (at 23°C, 24hrs) ¹¹	0.06	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.2 - 0.5	%	SABIC method
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Density ¹¹	1.25	g/cm³	ISO 1183
Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹	3.5	g/10 min	ASTM D1238
Water Absorption (at 23°C, saturated) ¹¹	0.22	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹	0.04	%	ISO 62-4
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.07	%	ISO 62
Melt Volume Rate (at 280°C, 10.0 kg) ¹¹	12	cm³/10 min	ISO 1133
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹	3	cm³/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	132	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.000036	1/°C	ASTM E831
Relative Temperature Index (Electrical) ᵖ ¹¹	110	°C	UL 746B
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.00003	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.00005	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.00005	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000025	1/°C	ASTM E831
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	105	°C	UL 746B
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000075	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000068	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000068	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	7.50E-05	1/°C	ASTM E831
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	110	°C	UL 746B
Thermal Conductivity ¹¹	0.28	W/m-°C	ISO 8302
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.00003	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.00007	1/°C	ISO 11359-2
Ball Pressure Test (at 123°C to 127°C) ¹¹	Pass	—	IEC 60695-10-2
Ball Pressure Test (approximate maximum) ¹¹	135	°C	IEC 60695-10-2
Vicat Softening Temperature (Rate B/50) ¹¹	142	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	142	°C	ASTM D1525
Vicat Softening Temperature (Rate B/50) ¹¹	140	°C	ISO 306
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	142	°C	ASTM D648
Vicat Softening Temperature (Rate A/50) ¹¹	150	°C	ISO 306
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	134	°C	ASTM D648
Vicat Softening Temperature (Rate B/120) ¹¹	145	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	144	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	135	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	130	°C	ISO 75/Ae
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	133	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Dielectric Strength (in oil, at 3.2mm) ¹¹	16	kV/mm	IEC 60243-1
Dielectric Strength (in oil, at 3.2mm) ¹¹	23.6	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	3	—	IEC 60250
Relative Permittivity (50/60 Hz) ¹¹	2.98	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.0016	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.004	—	IEC 60250
High Voltage Arc Track Rate (PLC) ¹¹	4	PLC Code	UL 746A
High Voltage Arc Track Rate (PLC) ¹¹	3	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ¹¹	3	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ¹¹	2	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ¹¹	1	PLC Code	UL 746A
High Ampere Arc Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 0) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 0) ¹¹	min. 0.71	mm	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	6	PLC Code	ASTM D495
Volume Resistivity ¹¹	1.00E+15	Ω.cm	IEC 60093
Volume Resistivity ¹¹	2.04E+16	Ω.cm	ASTM D257
Volume Resistivity ¹¹	2.04E+16	Ω.cm	IEC 60093
Surface Resistivity (ROA) ¹¹	min. 1.E+15	Ω	IEC 60093
Surface Resistivity (ROA) ¹¹	1.34E+17	Ω	IEC 60093
Surface Resistivity ¹¹	1.34E+17	Ω	ASTM D257
Dielectric Strength (in oil, at 0.8mm) ¹¹	30	kV/mm	IEC 60243-1
Dielectric Strength (in oil, at 1.6mm) ¹¹	25	kV/mm	IEC 60243-1
Dielectric Strength (in oil, at 1.6mm) ¹¹	26.2	kV/mm	ASTM D149
Relative Permittivity (1 MHz) ¹¹	2.9	—	IEC 60250
Relative Permittivity (1 MHz) ¹¹	2.93	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.002	—	IEC 60250
Dissipation Factor (at at 1 MHz) ¹¹	0.0034	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.0034	—	IEC 60250
Dielectric Strength (in oil, at 1.5mm) ¹¹	26.2	kV/mm	IEC 60243-1
Comparative Tracking Index ʳ ¹¹	225	V	IEC 60112
High Ampere Arc Ignition (PLC 3) ¹¹	min. 6	mm	UL 746A
High Ampere Arc Ignition (PLC 4) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 4) ¹¹	min. 0.4	mm	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 0.4	mm	UL 746A

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	100	J/m	ASTM D256
Izod Impact (Notched, at 23°C) ¹¹	106	J/m	ASTM D256
Izod Impact (Notched, at -40°C) ¹¹	96	J/m	ASTM D256
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	28	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹	27	kJ/m²	ISO 180/1U
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	30	kJ/m²	ISO 179/1eU
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	30	kJ/m²	ISO 179/1eU
Izod Impact (Unnotched, at 23°C) ¹¹	520	J/m	ASTM D4812
Izod Impact (Notched, at -30°C) ¹¹	90	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	18	J	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	9	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹	8	kJ/m²	ISO 180/1A
Charpy Impact (Notched, at 23°C) ¹¹	7	kJ/m²	ISO 179/2C

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	100 - 120	°C	—
Drying Temperature ⁷	110 - 120	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Drying Time ⁷	2 - 3	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Melt Temperature ⁷	280 - 300	°C	—
Melt Temperature ⁷	300 - 325	°C	—
Maximum Moisture Content ⁷	0.02	%	—
Nozzle Temperature ⁷	260 - 280	°C	—
Nozzle Temperature ⁷	300 - 325	°C	—
Front - Zone 3 Temperature ⁷	280 - 300	°C	—
Front - Zone 3 Temperature ⁷	290 - 325	°C	—
Middle - Zone 2 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	275 - 320	°C	—
Rear - Zone 1 Temperature ⁷	240 - 260	°C	—
Rear - Zone 1 Temperature ⁷	265 - 315	°C	—
Hopper Temperature ⁷	60 - 80	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Mold Temperature ⁷	80 - 120	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	20 - 100	rpm	—
Shot to Cylinder Size ⁷	30 - 70	%	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94-5VA Flame Class Rating) ʳ	min. 2	mm	UL 94
UL Recognized (94-5VA Flame Class Rating) ʳ	min. 2.5	mm	UL 94
UL Recognized (94V-0 Flame Class Rating) ʳ	min. 6	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ʳ	min. 1.5	mm	UL 94
UL Recognized (94V-1 Flame Class Rating) ʳ	min. 0.4	mm	UL 94
Glow Wire Flammability Index (at 1 mm) ʳ	960	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 1.5 mm) ʳ	960	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 2 mm) ʳ	960	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature (at 1.0 mm) ʳ	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 1.0 mm) ʳ	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 1.5 mm) ʳ	750	°C	IEC 60695-2-13
UV-light (Water exposure/immersion) ʳ	F1	—	UL 746C
UV-light (Water exposure/immersion) ʳ	F2	—	UL 746C
Oxygen Index (LOI) ʳ	30	%	ISO 4589
Oxygen Index (LOI) ʳ	30.9	%	ASTM D2863
Glow Wire Ignitability Temperature (at 2.0 mm) ʳ	800	°C	IEC 60695-2-13

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America