Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 50 | mg/1000cy | SABIC method |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 74 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 75 | MPa | ISO 527 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 119 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3990 | MPa | ASTM D790 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2.5 | % | ISO 527 |
| Hardness (Rockwell L) ¹¹ | 104 | — | ASTM D785 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4000 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 110 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 3000 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 100 | MPa | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.16 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.22 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.22 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
| Density ¹¹ | 1.17 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.07 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 10.0 kg) ¹¹ | 15 | cm³/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 140 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 147 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 131 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 110 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 110 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 1.10E+02 | °C | UL 746B |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000055 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000055 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ISO 11359-2 |
| Thermal Conductivity ¹¹ | 0.27 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00005 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Ball Pressure Test (approximate maximum) ¹¹ | 135 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 145 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 145 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 140 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 135 | °C | ISO 75/Ae |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | ASTM D257 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.8 | — | IEC 60250 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Relative Permittivity (1 MHz) ¹¹ | 3 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0017 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.005 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.003 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.0016 | — | ASTM D150 |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 0.8 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 0.71 | mm | UL 746A |
| Hot Wire Ignition (PLC 1) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 1) ¹¹ | min. 0.8 | mm | UL 746A |
| Hot Wire Ignition (PLC 1) ¹¹ | min. 0.71 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 3.30E+01 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 1.60E+01 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index ¹¹ | 250 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 96 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 69 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*3, at -40°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 5 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -40°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 5 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 105 - 110 | °C | — |
| Drying Temperature ⁷ | 100 - 120 | °C | — |
| Drying Time ⁷ | 3 - 4 | Hrs | — |
| Drying Time ⁷ | 2 - 3 | Hrs | — |
| Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
| Melt Temperature ⁷ | 280 - 310 | °C | — |
| Melt Temperature ⁷ | 280 - 300 | °C | — |
| Maximum Moisture Content ⁷ | 0.02 | % | — |
| Nozzle Temperature ⁷ | 280 - 310 | °C | — |
| Nozzle Temperature ⁷ | 260 - 280 | °C | — |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
| Front - Zone 3 Temperature ⁷ | 270 - 310 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 260 - 280 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 260 - 305 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 240 - 260 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 250 - 300 | °C | — |
| Hopper Temperature ⁷ | 60 - 80 | °C | — |
| Mold Temperature ⁷ | 80 - 120 | °C | — |
| Mold Temperature ⁷ | 75 - 105 | °C | — |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
| Screw Speed ⁷ | 20 - 100 | rpm | — |
| Shot to Cylinder Size ⁷ | 30 - 70 | % | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.8 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ʳ | min. 0.44 | mm | UL 94 |
| Oxygen Index (LOI) ʳ | 30 | % | ISO 4589 |
| Oxygen Index (LOI) ʳ | 33.9 | % | ASTM D2863 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |
| UV-light (Water exposure/immersion) ʳ | F2 | — | UL 746C |
| Glow Wire Flammability Index (at 1 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Needle Flame Test (10s, passes) ʳ | 1.5 | mm | IEC 60695-2-2 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.5 mm) ʳ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability