Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- CASE Ingredients Functions
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
- CASE Ingredients Features
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Typical Physical Properties
Value | Units | Test Method / Conditions | |
Adhesion to PA12 | 60 | N/cm | Initial |
Flexural Modulus | 1220 | MPa | ASTM D-790 |
Izod Impact Strength (at 23°C) | No Break | J/m | ASTM D-256 |
Melt Flow Rate | 20 | g/10 min | ASTM D-3307 |
Melting Point | 240 | °C | DSC |
Permeation Rate (CE10, at 60°C) | 2 | g-mm/m²-day | JIS Z0208 (CUP) |
Specific Gravity | 1.77 | — | ASTM D-792 |
Surface Resistivity | 1 x 10³ | Ω/square | AGC Method |
Tensile Elongation | 350 | % | ASTM D-638 |
Tensile Strength | 36 | MPa | ASTM D-638 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Processing
- Fluon LM-ETFE fluoropolymer resins can be processed using conventional melt processable techniques including extrusion, injection molding, blow molding, compression molding, and transfer molding. It is strongly recommended that process equipment exposed to molten resin be made of corrosion-resistant metals such as Monel, Inconel, or Hastelloy.
- Extruder barrels should be long relative to diameter (24/1 to 30/1 and beyond) and heaters should have adequate capacity to heat the material to approximately 340°C. Temperature controllers should be of the proportional-integral derivative (PID) type to insure precise temperature control. Extruder screws with a 3/1 compression ratio, a relatively long feed zone, and a ½ to 3 turn transition zone are recommended.
Storage & Handling
- Handling Precautions
- WARNING: Vapors that can be hazardous if inhaled may be liberated during processing.
- Please consult the Material Safety Data Sheet for Fluon LM-ETFE prior to use. It is also recommended that the user consult the latest edition of the “Guide to the Safe Handling of Fluoropolymer Resins” published by the Fluoropolymers Division of the Society of the Plastics Industry (SPI) for important handling and ventilation recommendations. Both publications are available from your AGC Chemicals Americas representative.
- Storage
The properties of Fluon LM-ETFE are not impacted by storage time. Storage and handling facilities should be designed to minimize contact with airborne contamination and the formulation of condensation on the resin. Fluoropolymers are not hydroscopic and will not typically need to be dried prior to use. However, masterbatches used to pigment fluoropolymers may contain materials that do absorb water and should be dried prior to use.