Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Injection Molding)
- Tribological Properties
- Rheological Properties
Value | Units | Test Method / Conditions | |
Flexural Modulus | 8600.0 | MPa | ISO 178 |
Flexural Strength | 175.0 | MPa | ISO 178 |
Tensile Modulus | 9800.0 | MPa | ISO 527 |
Tensile Strength at Break | 115.0 | MPa | ISO 527 |
Tensile Elongation at Break | 2.6 | % | ISO 527 |
Impact Strength (Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
Notched Impact Strength (Charpy, at 23°C) | 9.0 | kJ/m² | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Density | 1630.0 | kg/m³ | ISO 1183 |
Value | Units | Test Method / Conditions | |
Vicat B50 | 212.0 | °C | ISO 306 |
HDT / A (1.8 MPa) | 214.0 | °C | ISO 75-1/-2 |
DSC (Melt Point) | 227.0 | °C | ISO 11357 |
Value | Units | Test Method / Conditions | |
Melt Temperature | 250 - 270 | °C | — |
Mould Temperature | 80 - 120 | °C | — |
Value | Units | Test Method / Conditions | |
Coefficient of Sliding Friction µ (pv = 5*1 MPa*m/s) | 0.28 | — | ASTM G 137 |
Coefficient of Sliding Friction µH (pv = 5*1 MPa*m/s) | 0.19 | — | ASTM G 137 |
Specific Wear Rate ws (pv = 5*1 MPa*m/s) | 1.2 | E⁻⁶ mm³/Nm | ASTM G 137 |
Linear Wear Rate w (pv = 5*1 MPa*m/s) | 21.0 | µm/h | ASTM G 137 |
Value | Units | Test Method / Conditions | |
Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |
Regulatory & Compliance
Technical Details & Test Data
- Pre-Drying Conditions
- In a dry air (dessiccant) dryer 100-120 °C for 2-4 h
- In an air circulatIng dryer 100-120 °C for 4-8 h
- Dependant on moisture content
Storage & Handling
- Storage Conditions
Store in dry, protected from light not above 30°C.