PEXIDAN® L/T-UV is a high density PEX system consisting of a silane grafted basecompound A-1001 and a catalyst masterbatch CAT-003 (or A-1022 and CAT-117). When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN® L/T is listed by NSF International to standards 14 and 61 and to Canadian Standards Association standard B137.5. NSFI certification to ASTM F876 and ASTM F2023 testifies to its superior resistance to oxidation by hot, chlorinated water. PEXIDAN® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material.

PEXIDAN® J/T is a low density flame-retardant XLPE system curable by moisture and consists of a silane pregrafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-012FR. Mixed and extruded in the proper proportions (60:40), the two components result in a material that is curable by exposure to 70-95°C hot water or even ambient moisture. PEXIDAN® J/T is designed to meet SAE J1128 standards for GXL, TXL and SXL type insulation. PEXIDAN® J/T is halogenated but is RoHS-compliant.

PEXIDAN® X/T-UV is a low density flame-retardant XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-005FR-UV1. Mixed and extruded in the proper proportions the two-component system results in a material that is curable by exposure to 70-95°C hot water or even ambient moisture. PEXIDAN® X/T-UV is halogenated but is RoHS-compliant. UL44 type insulation may be marked SUNRES or SR in all colors for sizes of 6 AWG and larger. UL4703 photovoltaic insulation may be marked SUNRES in all sizes and colors

EXTINITY® 0202-103 is a highly loaded masterbatch of brominated flame retardant pre-dispersed in a polypropylene carrier. It has been designed for use in variety of compounding applications. The pellet form makes the flame retardant easier to handle, more efficient, and can lower overall costs. The product is RoHS compliant.

LINXIDAN® LX4433 is a Maleated HDPE Coupling Agent designed specifically to chemically bind natural fibers to HDPE in Wood-Plastic Composites. Coupling fibers to the HDPE matrix, in a 50% wood-filled system, reduces moisture uptake while increasing flexural modulus by 20% and overall flexural strength by 90%.

EXTINITY® 0202-102 is 48% active flame retardant masterbatch additive dispersed in co-polymer polypropylene (coPP) carrier. EXTINITY® 0202-102 can be added to polypropylene base resin and achieve flame retardant performance to meet UL vertical burn performance (UL V-0 and UL V-2).

EXTINITY® 0101-108 is a halogenated, flame retardant compound specifically designed for use in plenum tube applications. This compound has good thermal stability and can be converted easily on standard processing equipment.

PEXIDAN® V/T-2 is a low density flame-retardant XLPE system curable by moisture and consists of a silane-grafted base compound A-3001 and a catalyst masterbatch CAT-045FR. Mixed and extruded in the proper proportions (50/50), the two components result in a material that is curable by exposure to hot water. PEXIDAN® V/T-2 is halogenated but is RoHS-compliant.

PEXIDAN® H/T is a low density flame-retardant XLPE system curable by moisture and consists of a silane pregrafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-012FR. Mixed and extruded in the proper proportions (67/33) this mixture results in a material curable by exposure to 70-95°C hot water or even ambient moisture. PEXIDAN® H/T is listed with CSA for AWM and CL1251, CL1252 & CL1503, and for UL AWM styles 3173 and 3321. See below for a more complete list of suitable AWM styles. PEXIDAN® H/T is halogenated but is RoHS-compliant.

PEXIDAN® V/T is a low density flame-retardant XLPE system curable by moisture and consists of a silanegrafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-010FR. Mixed and extruded in the proper proportions (50/50), the two components result in a material that is curable by exposure to hot water. PEXIDAN® V/T is halogenated but is RoHS-compliant.

PEXIDAN® SX546 pre-grafted base is mixed with crosslinking catalyst masterbatch CM493CD, for small cross sections, or CM497CD, in the ratio 95:5, for a 125ºC working temperature system. This system has ambient cure.

LINXIDAN® LX4436 is a maleated polyolefin Coupling Agent designed for alloying dissimilar materials to improve physical properties. Suggested loading levels are between 1 and 4 wt% depending on the specific materials being compounded, particular physical property of interest and level of improvement desired in the identified property.

LINXIDAN® LX4520 is a polyolefin copolymerized with a siloxane functionality, designed to improve compatibility and mechanical properties of polymer compounds.

THERMODAN® HF TP832BUT has been developed specially to comply with the requirements of BS7655 Section 6 for types LTS1, 2, 3 and 4; EN 50290-2-27 for type HM2 and HD 604 for type HM4. Cables sheathed with TP832 have received LPCB approval.

THERMODAN® HF TP519C has been developed specially to offer good processability, very fast extrusion process with very low die drool.

THERMODAN® HF TP521NU has been developed specially to comply with the requirements of BS7655 Section 6 for types LTS1, 2, 3 and 4; EN 50290-2-27 for type HM2 and HD 604 for type HM4. Cables made with TP521 have passed the 3m3 smoke density chamber test to IEC 61034-2.

THERMODAN® HF TP519CBU has been developed specially to offer good processability, very fast extrusion process with very low die drool.

THERMODAN® HF TP812NU has been developed specially to offer good processability, fast extrusion process with very low die drool. TP812 is capable of meeting the flame retardant requirements of UL 1666, UL 1685, IEEE 1202, FT-4 in specific fiber optic constructions. It is also recognized as halogen free under UL 2885. It can be extruded using PVC extruders and screws. It possesses excellent tensile and flame retardant properties and meets the requirements of limited toxic and corrosive fume emission

EXTINITY® 0101-205 is a natural, non-halogen flame retardant RoHS polyolefin compound. It is designed for use in a wide variety of jacketing and coating applications. This compound has superior fire performance; including slow flame propagation, self-extinguishing characteristics, and low smoke production. EXTINITY® 0101-205 should be extruded with a screw configuration designed to optimize process conditions and throughput.

THERMODAN® HF TP835 has been developed specially to comply with the requirements of BS7655 Section 6 for types LTS1, 2, 3 and 4; EN 50290-2-27 for type HM2 and HD 604 for type HM4. Cables made with TP835 have passed the 3m3 smoke density chamber test to IEC 61034-2.

THERMODAN® HF TP519CB has been developed specially to offer good processability, very fast extrusion process with very low die drool.

PEXIDAN® SX409NT pre-grafted base is mixed with a crosslinking catalyst masterbatch CM401 in the ratio 95:5. The SX409NT:CM401 system has been developed specifically for cables operating up to 36kV. The graft compound contains a non-staining stabilizer and an effective tree retarder, giving outstanding long term retention of dielectric strength. This compound is typically used in conjunction with crosslinkable semi-conducting material for conductor and insulation shields. Crosslinking is obtained by exposure to moist or hot water immersion only.

THERMODAN® HF TP 543CBU has been developed specially to comply with the requirements of BS7655- 6.1 for types LTS1, 3 and 4; EN 50290-2-27 and HD 604 for type HM2 and HD 604 for type HM4. Cables made with TP543C have complied with IEC 60332, part 22, 23 & 24 – 1 and 3 fire tests.

PEXIDAN® HF SX612ES pre-grafted base is mixed with catalyst masterbatch CM602 or CM601, in an addition rate between 5% and 10%, depending on extrusion conditions. This system has ambient cure. PEXIDAN® HF SX612ES has been designed to meet the requirements of IEC 60092-351 HF90, EN 50363-5, EI5 type, EN 50525-1 and EN 50525-3-41, with enhanced fire resistance to comply with fire testing on smaller cross sections.

THERMODAN® HF TP 543CBT has been developed specially to comply with the requirements of BS7655- 6.1 for types LTS1, 3 and 4; EN 50290-2-27 and HD 604 for type HM2 and HD 604 for type HM4. Cables made with TP543C have complied with IEC 60332, part 22, 23 & 24 – 1 and 3 fire tests.

THERMODAN® HF TP812BU has been developed specially to offer good processability, fast extrusion process with very low die drool. TP812 is capable of meeting the flame retardant requirements of UL 1666, UL 1685, IEEE 1202, FT-4 in specific fiber optic constructions. It is also recognized as halogen free under UL 2885. It can be extruded using PVC extruders and screws. It possesses excellent tensile and flame retardant properties and meets the requirements of limited toxic and corrosive fume emission

PEXIDAN® L/T ECLIPSE is a high density PEX system consisting of a silane grafted basecompound A-1001 and a catalyst masterbatch CAT-003 (or A-1022 and CAT-117). When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN® L/T is listed by NSF International to standards 14 and 61 and to Canadian Standards Association standard B137.5. NSFI certification to ASTM F876 and ASTM F2023 testifies to its superior resistance to oxidation by hot, chlorinated water. PEXIDAN® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material.

EXTINITY® 0201-312 is a highly loaded antimony trioxide concentrate that can be used for a variety of applications including film, sheet, and extrusion coating. The content of antimony trioxide in EXTINITY® 0201-312 is 80%, by weight. Use of EXTINITY® 0201-312 eliminates the exposure hazards typically associated with handling antimony trioxide powder, since all of the antimony trioxide powder is dispersed, distributed and encapsulated in a LDPE carrier resin.

THERMODAN® HF TP870BU has been developed specially to meet general requirements of BS 7655 Section 6.1 type LTS 1.

THERMODAN® HF TP519C has been developed specially to offer good processability, very fast extrusion process with very low die drool.

PEXIDAN® X/T is a low density flame-retardant XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame retardant catalyst masterbatch CAT-005FR. Mixed and extruded in the proper proportions (80:20), the two components result in a material that is curable by exposure to 70-95°C hot water or even ambient moisture. In order to prevent pre-scorching the grafted compound and the catalyst masterbatch must be stored separately and mixed only when used. PEXIDAN® X/T is halogenated but is RoHS compliant.

LINXIDAN® LX4510 is a polyolefin plastomer with a silane copolymer functionality, designed to improve compatibility and mechanical properties of polymer compounds. Contrarily to conventionally maleated polyolefin coupling agents, LINXIDAN® LX4510 does not interfere with metal stearates used as lubricants in Wood Plastics Composites (WPC), providing increased tensile strength, impact strength and flexural modulus, and reduced moisture absorption.

THERMODAN® HF TP870NU has been developed specially to meet general requirements of BS 7655 Section 6.1 type LTS 1.

PEXIDAN® SX522A pre-grafted base is mixed with crosslinking catalyst masterbatch CM401 in the ratio 95:5. This system has ambient cure.

PEXIDAN® SX523 pre-grafted black base is mixed with crosslinking catalyst masterbatch CM493 or CM497 in the ratio 95:5. This system is carbon loaded, with high UV stabilization, and has been developed especially for usage on overhead power cables insulation according NFC 33-209, “Câble Torsadé”. Crosslinking is obtained by exposure to moist or hot water immersion only.

Material SX739 is a silane grafted HDPE compound curable by exposure to moist conditions. SX739 is specifically designed for high output processing by conventional thermoplastic injection molding. The graft component SX739 is mixed with a crosslinking catalyst masterbatch CM488/6 generally in the ratio 95:5. This material combines good flow, high rigidity and excellent notched impact strength. The two component system SX739:CM488/6 has high degree of crosslinking which gives it a useful strength at temperatures not usually reached by HDPE.