Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
Applications & Uses
- Markets
- Applications
- Application Area
- Compatible Substrates & Surfaces
- Cure Method
- Application Details
- The substrate areas that will be in contact with the sealant must be clean, dry and free of all loose material such as dust, dirt, rust, oil and other contaminants. Non-porous substrates should be cleaned with a solvent and a clean, lint-free, cotton cloth. Remove residual solvent before it evaporates with a fresh clean, dry cloth.
- For application from cartridges cut thread open, fix nozzle on top and cut to required bead size. The sealant can be applied in beads or layers. It requires moisture in order to cure. The curing time can take longer at lower temperatures, lower humidity or by low volume of air exchange.
Adhesion
WACKER® 130 - GLASS AND GLAZING exhibits excellent primerless adhesion to most non-porous siliceous material, e.g. glass, tiles, ceramics, enamel, glazed tiles and clinker Users must carry out their own tests due to the great variety of substances. The adhesion can be improved in many cases by pretreatment of the substrates with a primer.
Properties
- Cured Properties
Value Units Test Method / Conditions Modulus (at 100 % elongation, joint) 0.38 N/mm² ISO 8339-A Modulus (at 100 % elongation, S2-dumbbell) 0.35 N/mm² ISO 37 Movement Capability 25 % - Shore Hardness A 18 - ISO 868 Tensile Strength (Joint) 0.6 N/mm² ISO 8339 Tensile Strength (S2-dumbbell) 1.8 N/mm² ISO 37 Ultimate Elongation (joint) 200 % ISO 8339-A Ultimate Elongation (S2-dumbbell) 550 % ISO 37 - Uncured Properties
Value Units Test Method / Conditions Consistency Non-sag - ISO 7390, Profile U 20 Density (at 23°C, 1013 hPa) 1 g/cm³ ISO 1183-1 A Extrusion Mass Flow Rate (at 6 bar) 250 - 850 g/min - Skin Formating Time (at 23°C, 50% r.h) 20 minutes Internal method - Properties
- Solvent free
- Non-sag
- Excellent tooling characteristics for professional use
- Readily gunnable both at low (+5 °C) and high (+40 °C) temperatures
- Rapid crosslinking: quickly becomes tack-free and crack resistant
- Flexible at low (- 40 °C) and high temperatures (+ 100 °C) after curing
- Long shelf life
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Packaging & Availability
- Country Availability
- Packaging Type
- Regional Availability
- Packaging Information
WACKER® 130 - GLASS & GLAZING 7 is usually supplied in standard size cartridges that fit all standard caulking guns.