Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Typical Properties
- Optical Properties
- Flammability
- Processing Information (Injection Molding)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Flexural Modulus | 5800.0 | MPa | ISO 178 |
| Flexural Strength | 150.0 | MPa | ISO 178 |
| Tensile Modulus | 6000.0 | MPa | ISO 527 |
| Tensile Strength at Break | 95.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.7 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Value | Units | Test Method / Conditions | |
| Density | 1340.0 | kg/m³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Vicat B50 | 145.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 140.0 | °C | ISO 75-1/-2 |
| Value | Units | Test Method / Conditions | |
| Moisture Content | max. 0.02 | % | - |
| Value | Units | Test Method / Conditions | |
| Total Transmission T(Y) (d=1,0mm, A, 2°) | 53.0 | % | ISO 13468 |
| Total Transmission T(Y) (d=2,0mm, A, 2°) | 37.0 | % | ISO 13468 |
| Total Transmission T(Y) (d=3,0mm, A, 2°) | 27.0 | % | ISO 13468 |
| Total Transmission T(Y) (d=4,0mm, A, 2°) | 21.0 | % | ISO 13468 |
| Haze T(Y) (d=1.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Haze T(Y) (d=2.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Haze T(Y) (d=3.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Haze T(Y) (d=4.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Half Power Angle T(Y) (d=1mm, A, 2°) | 47.0 | Degree | - |
| Half Power Angle T(Y) (d=2mm, A, 2°) | 60.0 | Degree | - |
| Half Power Angle T(Y) (d=3mm, A, 2°) | 62.0 | Degree | - |
| Half Power Angle T(Y) (d=4mm, A, 2°) | 63.0 | Degree | - |
| Value | Units | Test Method / Conditions | |
| Flammability (0.75 m) | V - 2 | class | UL 94 |
| Flammability (1.5 mm) | HB | class | UL 94 |
| Glow Wire (GWFI, 850°C, 1mm) | Passed | - | DIN EN 60695 |
| Glow Wire (GWFI, 850°C, 2mm) | Passed | - | DIN EN 60695 |
| Value | Units | Test Method / Conditions | |
| Melt Temperature | 290 - 320 | °C | - |
| Mould Temperature | 80 - 130 | °C | - |
| Value | Units | Test Method / Conditions | |
| Melt Index (MVR) | 11.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | - |
| MVR Load | 1.2 | kg | - |
| Shrinkage (Lengthwise, 24h) | 0.4 - 0.7 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.4 - 0.8 | % | ISO 294-4 |
Regulatory & Compliance
Technical Details & Test Data
- Pre-Drying Conditions
120 °C in a dry air (dessiccant) dryer for 2-3 h
Storage & Handling
- Storage Conditions
Store in dry, protected from light.