VINNAPAS® EP 705A (ULS) is a vinyl acetate-ethylene copolymer specifically designed as a base polymer for high-performance adhesives. It is produced without using formaldehyde donors. The low viscosity of VINNAPAS® EP 705A (ULS) and its excellent Newtonian flow behavior make it well-suited for high-speed packaging machines.

Brand: VINNAPAS (218 products)

Chemical Family: Vinyl Acetate Ethylene (VAE) Copolymer

End Uses: Extrusion Coating

Compatible Substrates & Surfaces: Elastomers & Rubbers, Paper, Textiles, Wood

Glass Transition Temperature (Tg): 0.0 - 0.0 °C

Features: Frost Resistance, Good Chemical Stability, High Performance

Technical Data Sheet
Enhanced TDS

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Features & Benefits

Applications & Uses

Application Method
Compatible Polymers & Resins
Compatible Substrates & Surfaces
Coating Type
  • Film-to-Wood lamination
  • Paper Packaging & Converting
Application Details

VINNAPAS® EP 705A (ULS) forms strong bonds between porous substrates and various films. VINNAPAS® EP 705A (ULS) bonds such widely diversified substrates as paper, wood, cotton cloth, nylon cloth, hardboard, urethane foam and certain types of coated paperboard. Typical application fields of VINNAPAS® EP 705A (ULS) are as follows:

  • Packaging (window cartons and carton forming)
  • Luggage and handbags
  • Envelop and bookbinding
  • Textiles or upholstery

It has a good stability at high-speed machines and is suitable for either of roll, extruder or spray application.


Physical Form
Typical Properties
ValueUnitsTest Method / Conditions
Appearance of the Dispersion FilmClear glossy-Visual
Density (at 20°C)approx. 1.07 g/cm³Specific method
Filler and Pigment CompatibilityVery good-Specific method
Glass Transition Temperatureapprox. 0 °CSpecific method
Minimum Film Forming Temperature0°CSpecific method
Predominant Particle Sizeapprox. 1 µmSpecific method
Protective Colloid (Emulsifier System)PVOH--
Surface of the Dispersion FilmSlight tack-Specific method
ValueUnitsTest Method / Conditions
Dynamic Viscosity (at 25°C)1900 - 2800 mPa·sSpecific method
pH4.0 - 6.0-Specific method
Solids Content54 - 56 %Specific method
  • VINNAPAS® EP 705A (ULS) is chemically stable at both high and low pH.
  • It is compatible with other polyvinyl acetate (PVAc) polymers, rubber lattices, EVCL dispersions and VINNAPAS® VAE dispersions.
  • It is also compatible with an assortment of resins, solvents, plasticizers and other modifiers.

Packaging & Availability

Storage & Handling

Shelf Life
9 Months
Storage Information
  • When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 9 months starting from the date of manufacture if stored in the original, unopened containers at temperatures between 5 and 30°C. 
  • Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended.
  • As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.

Preservation for Transport, Storage and further Processing

  • The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms.
  • The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10-20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations.
  • Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed. Finished products manufactured from polymer dispersions usually also require preservation.
  • The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.