Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Specific Features
- Low coefficient of friction
- Self-adhesive
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Applications
- Battery
- Connector Seals
- General Automotive Parts
- Molded Parts
- Molded Seals (Automotive)
- Application Details
Selfbonding ELASTOSIL® LR 3675 grades adhere to various plastic substrates (e. g. PA, PBT) and metals, but not to the mold. Because of the individual surface properties adhesion to the substrate must be tested before production. ELASTOSIL ® LR 3675 can generally be used for technical applications without post-curing, e.g. connector seals in the automotive industry.
Processing
The A and B components are delivered ready to use in 20 and 200 liter drums. With adequate metering equipment, they can be pumped directly from the original containers into the injection molding machine and mixed by a static mixer. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days. Start-up of new molds should be supported by use of ELASTOSIL® AUX Mold Release Agent 32.
Properties
- Physical Form
- Cured Properties
Value Units Test Method / Conditions Compression Set (at 22 hours, 125°C) 12 % DIN ISO 815-1 type B method A Compression Set (at 22 hours, 150°C) 23 % DIN ISO 815-1 type B method A Density 1.12 g/cm³ DIN EN ISO 1183-1 A Elongation (at break) 410 % ISO 37 Type 1 Shore Hardness A 50 - DIN ISO 48-4 Tear Strength 33 N/mm ASTM D 624 B Tensile Strength 7.8 N/mm² ISO 37 Type 1 - Uncured Properties
Value Units Test Method / Conditions Dynamic Viscosity (Shear rate 1 s⁻¹) 1600000 mPa·s DIN EN ISO 3219 Dynamic Viscosity (Shear rate 10 s⁻¹) 480000 mPa·s DIN EN ISO 3219 - Properties
ELASTOSIL® LR 3675 series are primerless, self-bonding grades that adhere to various plastic substrates (e.g. PA, PBT) and metals. The bonding is improved by a subsequent heat treatment process (e.g. one hour at 100°C) or by a longer storing at room temperature. The cured rubbers show a lower coefficient of friction without exuding oil as happens in oilbleeding silicone elastomers.
- Note
Cure conditions : 5 min / 165°C in press.
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Packaging & Availability
- Country Availability
- Packaging Type
- Regional Availability
- Packaging Information
This product is available in 20 kg pail and 200 kg drum kits.
Storage & Handling
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.