Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
Features & Benefits
- Labeling Claims
- Industrial Additives Features
Applications & Uses
- Applications
- Application Method
- Industrial Additives End Use
- Applications
- Woven Carpet
- Carpet
- Needlefelt Carpet
- Tufted Carpet Tiles
- Tufted Broadloom Carpet
- Application Details
General
- VINNAPAS® CA 5317 can be used in the production of woven carpets, needle felt floor coverings and tufted carpets, where it delivers high dry adhesion strength and imparts soft to medium hand.
- VINNAPAS® CA 5317 offers excellent adhesion to a variety of substrates together with high cohesion.
Special
- VINNAPAS® CA 5317 can be applied by a number of different application methods including foaming (direct coating), pan coating, saturation and spraying.
- VINNAPAS® CA 5317 performs well on various fiber types including polypropylene, polyamide, cellulose, and polyester.
ProcessingVINNAPAS® CA 5317 can take moderate filler loads with calcium carbonate or aluminum trihydrate (ATH) for compounding. Foaming additives and dispersing agents can be added to VINNAPAS® CA 5317 to improve foamability and filler acceptance. The compatibility and efficacy should be checked by conducting a storage stability test.
- Polymer Dispersions : VINNAPAS® CA 5317 is miscible in all portions with most VINNAPAS® dispersions. Here too, the compatibility of the mixture should be tested by conducting a storage test.
- Thickening agents : We recommend alkali-swellable poly(acrylic acid) derivatives. Products with neutral pH, e.g., those based on cellulose derivatives, poly(vinyl alcohol) or polyurethane, can also be considered. Their compatibility and efficacy should be evaluated.
- Mineral Fillers : VINNAPAS® CA 5317 is compatible with many common mineral fillers (chalk, gypsum, dolomite, aluminum hydroxide). The latter product is especially suitable for the production of low smoke emission flame-proofing compounds used in textile floor coverings. The compatibility and stability should be checked by conducting a storage test.
Properties
- Color
- Physical Form
- Typical Properties
- Specifications
- Properties
- VINNAPAS® CA 5317 may be used in applications where filler loadings of calcium carbonate, aluminum trihydrate (ATH) or other fillers are required.
- The films are noted for their flexibility to below freezing point, aging resistance and light stability.
- The dispersion is compatible with acrylic dispersions and many styrene-butadiene latices.
Value | Units | Test Method / Conditions | |
Density (at 23°C) | approx. 1.07 | g/cm³ | ISO 2811 |
Filler and Pigment Compatibility | Good | — | Specific method |
Glass Transition Temperature | approx. 3 | °C | Specific method |
Minimum Film Forming Temperature | 0 | °C | DIN ISO 2115 |
Predominant Particle Size | approx. 0.9 | µm | Specific method |
Value | Units | Test Method / Conditions | |
Dynamic Viscosity (at 23°C) | 2800 - 4800 | mPa·s | DIN EN ISO 2555 |
pH | 4 - 5 | — | DIN/ISO 976 |
Solids Content | 59 - 61 | % | DIN EN ISO 3251 |
Regulatory & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 6 Months
- Storage Information
- When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 6 months starting from the date of manufacture if stored in the original, unopened containers at temperatures between 5 and 30°C.
- Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended.
- As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.
Preservation for Transport, Storage and further Processing
- The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms.
- The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10-20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations.
- Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed. Finished products manufactured from polymer dispersions usually also require preservation.
- The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.