- ELASTOSIL® - Ready-to-Use Construction Sealants
- Sealants
- Application Details
Application Fields
- Sealing of connection and expansion joints in the building industry.
- Sealing of perimeter joints
- Sealing of joints between glazing and supporting structures (frames, transoms, mullions).
- Industrial application as sealant in the automotive, aircraft and shipbuilding industries.
Processing
The substrate areas that will be in contact with the sealant must be clean, dry and free of all loose material, dust, dirt, rust, oil and other contaminants. Non-porous substrates should be cleaned with a solvent and a clean, lint-free, cotton cloth. Remove residual solvent before it evaporates with a fresh clean, dry cloth.
Adhesion
ELASTOSIL® K760 C exhibits excellent primerless adhesion to many substrates, e.g. glass, tiles, ceramics, enamel, glazed tiles and clinker e.g. aluminum, steel, zinc or copper wood, and many plastics. Users must carry out their own tests due to the great variety of substances. The adhesion can be improved in many cases by pretreatment of the substrates with a primer.
Properties
- Typical Properties
- Cured Properties
- Uncured Properties
- Properties
- Fire retardant
- Excellent weatherability
- Excellent tooling characteristics for professional use
- Non-corrosive to metals
- Suitable for alkaline substrates such as concrete, mortar, fibrous cement
- Matt finish
- Excellent adhesion on most substrates without primer
- Solvent-free, thus featuring low volume shrinkage during vulcanization
- Ready gunnability at low (+ 5 °C) and high (+ 40 °C) temperatures
- Flexible at low (-40 °C) and high temperatures (+150 °C)
- Non-sag
| Value | Units | Test Method / Conditions | |
| Movement Capability | 25 | % | ISO 11600 |
| Movement Capability | 50 | % | ASTM C920 |
| Value | Units | Test Method / Conditions | |
| Modulus (at 100 % elongation) | 0.4 | N/mm² | ISO 8339-A |
| Movement Capability | 25 | % | ISO 11600 |
| Movement Capability | 50 | % | ASTM C920 |
| Shore Hardness A | 22 | — | ISO 868 |
| Tensile Strength | 0.5 | N/mm² | ISO 8339-A |
| Ultimate Elongation | 250 | % | ISO 8339-A |
| Value | Units | Test Method / Conditions | |
| Consistency | Non-sag | — | ISO 7390, Profile U 20 |
| Density (at 23°C) | 1.4 | g/cm³ | ISO 1183-1 A |
| Skin Formating Time (at 23°C, 50% r.h) | 20 | minutes | — |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Quality Standards
- Restrictions in Use
- ELASTOSIL® K760 C must not be used for insulating glass applications
- ELASTOSIL® K760 C must not be used for structural glazing bonding - it is the responsibility of the user to test the compatibility of the sealant with the adjoining materials.
- Incompatible substances like coating materials (paints, varnishes and glazes) or organic plasticizer containing rubbers (EPDM, butyl and neoprene) can lead to discoloration or other impairments like loss of adhesion of the sealant. Materials in direct contact with the applied sealant like cleaning agents and materials in indirect contact like gaseous emissions can damage the sealant in its function or change its appearance.
- Because of the multitude of these materials, Wacker cannot make a general statement to the compatibility of materials with the sealant. In case of doubt the user shall conduct appropriate preliminary tests.
- ELASTOSIL® K760 C is not recommended for use on natural stones, such as marble, granite, quartzite, as it can cause staining.
- ELASTOSIL® K760 C is not recommended for sealing of aquaria or for longer term use under water.
- ELASTOSIL® K760 C is not suitable for food grade applications where the joints are likely to come in contact with food.
- ELASTOSIL® K760 C is not suitable for use as a mirror adhesive - the time until complete curing may be extended at lower temperature, lower humidity, increasing film thickness or by low volume of air exchange - the use of tooling agents should be avoided if possible. Otherwise, water or a diluted solution of a little neutral soap or alcohol in water should be sparingly applied.
Safety & Health
- Safety Note
- During vulcanization methanol and ethanol are released. These vapors should not be inhaled for long periods or in high concentration. Hence, good ventilation of the work place is necessary.
- Should uncured silicone rubber come into contact with eyes or mucous membranes, the affected area must be rinsed thoroughly with water as irritation will otherwise be caused. Cured silicone rubber, however, can be handled without any risk to health. Keep away from children.