Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Special Features
- Oil resistant
- Ultra-low compression set
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- General Automotive Parts
- Molded Parts
- Roller Coatings
- Application Details
The compounds are recommended for all kinds of seals that come into contact with mineral oils. ELASTOSIL® R 701/60 OH is used especially when low compression set is crucial for achieving good seal properties. The compounds may also be used for making high quality silicone-rubber-covered rollers.
Processing
- ELASTOSIL® R 701/60 OH is suitable for compression, transfer and injection molding and also for making extruded profiles. ELASTOSIL® R 701/60 OH can be vulcanized with the peroxides normally used for compression molding or extrusion of solid silicone rubber.
Properties
- Oil Resistance Properties
- Cured Properties
- Properties
- Good heat- and reversion-stabilized.
- Excellent resistance to mineral oil.
- When Curing Agent E is used, blooming of the decomposition products will not occur.
- Good elasticity and low compression set, even when Curing Agent E is used.
Non-post-cure properties: The differences in the mechanical properties of post-cured and non-post-cured vulcanizates are only very slight.
- Note
Cure conditions: 0.7 % ELASTOSIL® AUX Crosslinker C1 (Dicumylperoxide), 15 min / 165 °C in press, post-cured 4 h / 200 °C.
| Value | Units | Test Method / Conditions | |
| Elongation (at break, 500 hours, 150°C, Lubrizol® OS 206 304) | 330 | % | ISO 37 |
| Elongation (at break, 70 hours, 150°C, IRM 901) | 350 | % | ISO 37 |
| Elongation (at break, 70 hours, 150°C, IRM 903) | 240 | % | ISO 37 |
| Shore Hardness A (500 hours, 150°C, Lubrizol® OS 206 304) | 42 | — | DIN ISO 48-4 |
| Shore Hardness A (70 hours, 150°C, IRM 901) | 66 | — | DIN ISO 48-4 |
| Shore Hardness A (70 hours, 150°C, IRM 903) | 45 | — | DIN ISO 48-4 |
| Tensile Strength (500 hours, at 150°C, Lubrizol® OS 206 304) | 6.2 | N/mm² | ISO 37 |
| Tensile Strength (70 hours, at 150°C, IRM 901) | 7.7 | N/mm² | ISO 37 |
| Tensile Strength (70 hours, at 150°C, IRM 903) | 5.8 | N/mm² | ISO 37 |
| Volume Change (at 150°C, 500 hours, Lubrizol® OS 206 304) | 21 | % | — |
| Volume Change (at 150°C, 70 hours, IRM 901) | 7 | % | — |
| Volume Change (at 150°C, 70 hours, IRM 903) | 46 | % | — |
| Value | Units | Test Method / Conditions | |
| Compression Set (Curing Agent C1, at 22 hours, 175°C) | 6 | % | DIN ISO 815-1 type B method A |
| Density (Curing Agent C1) | 1.24 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Curing Agent C1) | 340 | % | ISO 37 Type 1 |
| Rebound Resilience (Curing Agent C1) | 57 | % | ISO 4662 |
| Shore Hardness A (Curing Agent C1) | 61 | — | DIN ISO 48-4 |
| Tear Strength (Curing Agent C1) | 17 | N/mm | ASTM D 624 B |
| Tensile Strength (Curing Agent C1) | 7.6 | N/mm² | ISO 37 Type 1 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Packaging Information
This product is available in 20 kg and 540 kg cardboard packaging.
Storage & Handling
- Storage Information
Please store the cardboard boxes in a dry and cool place. Already opened boxes should be closed again to avoid any contamination.