Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Special Features
- Coolant resistant
- Food-contact
- Steam resistant
- Ultra-low compression set
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Dairy & Food Applications
- General Automotive Parts
- Molded Parts
- Household Applications
- Profiles & Tubings
- Application Details
- This compound can be used in the manufacture of molded parts, but also particularly extrusion, for producing profiles, e. g. for windows and facades.
- Provided appropriate processing, articles produced from ELASTOSIL® R 861/70 S can be used for food contact applications in accordance with the Recommendation "XV. Silicones" of the BfR and FDA 21 CFR 177.2600 under observance of any given limitations on extractable and volatile substances. Furthermore, the product contains low levels of residual toluene which has to be completely removed from the final food contact article.
Processing
- To obtain optimum compression set values it is advisable to post-cure for 4 hours at 200°C. We recommend to use 1.5 % Curing Agent E for the manufacture of extrudates, and 0.7 % C1 or 1.2 % C6 for molded parts.
Properties
- Coolant Resistance Properties
- Oil Resistance Properties
- Cured Properties
- Note
Cure conditions (post-cured 4 h / 200 °C):
- 1.5 % ELASTOSIL® AUX Crosslinker E (50% paste of bis-(2,4-dichlorobenzoyl)-peroxide in silicone fluid); 10 min / 135°C in press
- 0.7 % ELASTOSIL® AUX Crosslinker C1 (Dicumylperoxide); 15 min /165 °C in press.
Coolant Resstant Properties:
- After immersion in coolant
- 1000 h / 125 °C in autoclave
- Cure conditions: 0.7 % ELASTOSIL® AUX Crosslinker C1 (Dicumylperoxide), 15 min / 165 °C in press, post-cured 4 h / 200 °C.
Oil Resistance Conditions: 0.7 % ELASTOSIL® AUX Crosslinker C1 (Dicumylperoxide), 15 min / 165 °C in press, post-cured 4 h / 200 °C
| Value | Units | Test Method / Conditions | |
| Compression Set (post-cured 4hours, at 200°C, Glysantin® G48 / distilled water 50:50) | 89 | % | DIN ISO 815-1 type B method B |
| Elongation (at break, Glysantin® G48 / distilled water 50:50) | 230 | % | ISO 37 |
| Shore Hardness A (Glysantin® G40 / distilled water 50:50) | 80 | — | DIN ISO 48-4 |
| Tensile Strength (Glysantin® G48 / distilled water 50:50) | 6.3 | N/mm² | ISO 37 |
| Volume Change (Glysantin® G48 / distilled water 50:50) | -1 | % | — |
| Value | Units | Test Method / Conditions | |
| Elongation (at break, 70 hours, 150°C, IRM 901) | 260 | % | ISO 37 |
| Elongation (at break, 70 hours, 150°C, IRM 903) | 240 | % | ISO 37 |
| Shore Hardness A (70 hours, 150°C, IRM 901) | 73 | — | DIN ISO 48-4 |
| Shore Hardness A (70 hours, 150°C, IRM 903) | 54 | — | DIN ISO 48-4 |
| Tensile Strength (70 hours, at 150°C, IRM 901) | 7 | N/mm² | ISO 37 |
| Tensile Strength (70 hours, at 150°C, IRM 903) | 8.5 | N/mm² | ISO 37 |
| Volume Change (at 150°C, 70 hours, IRM 901) | 5 | % | — |
| Volume Change (at 150°C, 70 hours, IRM 903) | 43 | % | — |
| Value | Units | Test Method / Conditions | |
| Compression Set (Curing Agent C1, at 22 hours, 175°C) | 8 | % | DIN ISO 815-1 type B method A |
| Compression Set (Curing Agent C1, at 70 hours, 175°C) | 20 | % | DIN ISO 815-1 type B method A |
| Compression Set (Curing Agent E, at 22 hours, 175°C) | 31 | % | DIN ISO 815-1 type B method A |
| Compression Set (Curing Agent E, at 70 hours, 175°C) | 50 | % | DIN ISO 815-1 type B method A |
| Density (Curing Agent C1) | 1.16 | g/cm³ | DIN EN ISO 1183-1 A |
| Density (Curing Agent E) | 1.16 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Curing Agent C1) | 290 | % | ISO 37 Type 1 |
| Elongation (at break, Curing Agent E) | 320 | % | ISO 37 Type 1 |
| Rebound Resilience (Curing Agent C1) | 50 | % | ISO 4662 |
| Rebound Resilience (Curing Agent E) | 47 | % | ISO 4662 |
| Shore Hardness A (Curing Agent C1) | 73 | — | DIN ISO 48-4 |
| Shore Hardness A (Curing Agent E) | 73 | — | DIN ISO 48-4 |
| Tear Strength (Curing Agent C1) | 17 | N/mm | ASTM D 624 B |
| Tear Strength (Curing Agent E) | 18 | N/mm | ASTM D 624 B |
| Tensile Strength (Curing Agent C1) | 8.6 | N/mm² | ISO 37 Type 1 |
| Tensile Strength (Curing Agent E) | 8.8 | N/mm² | ISO 37 Type 1 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Packaging Information
This product is available in 20 kg and 540 kg cardboard packaging.
Storage & Handling
- Storage Information
Please store the cardboard boxes in a dry and cool place. Already opened boxes should be closed again to avoid any contamination.