Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Specific Features
- Addition Curing
- Food-contact
- Heat resistant
- High rebound resilience
- Two-component
- Ultra-low compression set
Applications & Uses
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Dairy Applications
- Household Applications
- Profiles & Tubings
- Application Details
ELASTOSIL® R plus 4350/55 is suited for the manufacture of extruded articles exhibiting excellent heat stability. Properly cured and post-cured vulcanizates of ELASTOSIL® R plus 4350/55 can be used for food contact applications and are suitable for use under the Recommendation "XV. Silicones" of the BfR and FDA 21 CFR §177.2600 "Rubber Articles Intended for Repeated Use" considering any given limitations on extractable and volatile substances.
Processing
- ELASTOSIL® R plus 4350 may not be cured with peroxides but only with the platinum catalyst batch ELASTOSIL® AUX Batch PT 1.
- ELASTOSIL® R plus 4350/55 and ELASTOSIL® AUX Batch PT 1 are mixed homogeneously on a roll mill in a ratio of 100:1.3 A higher catalyst dosage results in a faster curing but a reduced pot life.
- Care must be taken to keep the compound cool during mixing. A homogeneous incorporation is a must, but the temperature of the rubber should not exceed 30 °C, otherwise there is a risk of scorch.
- The cross linking reaction starts as soon as ELASTOSIL® AUX Batch PT 1 has been added. The rate and degree of crosslinking is dependent on storage time and temperature. At 23 °C the pot life is approximately 24 h. This can be extended by storing the catalyzed mixture at lower temperature.
Properties
- Cured Properties
- Properties
Cured articles made of ELASTOSIL® R plus 4350/55 exhibit excellent heat stability. Thanks to addition cure, the vulcanization reaction is significantly faster compared to peroxide curing materials. No peroxide decomposition products are formed during vulcanization. At service temperatures above approx. 180°C the addition of heat stabilizers is recommended.
- Note
Cure conditions: 1,3% ELASTOSIL® AUX PT 1, 15 min / 165°C in press, post-cure 4 h / 200°C.
Value | Units | Test Method / Conditions | |
Compression Set (at 22 hours, 175°C) | 10 | % | DIN ISO 815-1 type B method A |
Density | 1.13 | g/cm³ | DIN EN ISO 1183-1 A |
Elongation (at break) | 350 | % | ISO 37 Type 1 |
Rebound Resilience | 60 | % | ISO 4662 |
Shore Hardness A | 58 | — | DIN ISO 48-4 |
Tear Strength | 18 | N/mm | ASTM D 624 B |
Tensile Strength | 8.2 | N/mm² | ISO 37 Type 1 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Packaging Information
This product is available in 20 kg and 540 kg cardboard packaging.
Storage & Handling
- Storage Information
Please store the cardboard boxes in a dry and cool place. Once opened, cardboard boxes should always be resealed after use to avoid any contamination and to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.