POWERSIL® 466 LV A/B is suitable for production of electrically conductive injection molded articles, especially cable accessories in the medium and high voltage range. The range of use spreads from push-on accessories to cold shrink applications. POWERSIL® 466 LV A/B combines a low Shore A durometer with high elongation, good setting properties (low tension set) and good mechanical properties which are a must for cold shrink applications. POWERSIL® 466 LV A/B is a low viscosity LSR that shows excellent processing properties.
Processing
Components A and B are delivered ready to use in drums of 20 and 200 liters capacity. They can be pumped by means of standard metering equipment from these drums and mixing in a static mixer straight into the heated mold. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days.
Properties
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Ready-to-use, two-component system
- High elongation at break, low tension set
- Stable electrical properties
- Good mechanical properties
- Note
Cured Properties: Cure conditions: 5 min / 165°C and post-cured for 4 h at 200°C.
| Value | Units | Test Method / Conditions | |
| Dynamic Viscosity (A+B, Shear rate 10 s⁻¹) | 400000 | mPa·s | DIN EN ISO 3219 |
| Kick-Off Temperature (A+B) | 115 | °C | — |
| Pot Life (A+B, at 23°C) | 3 | days | — |
| Value | Units | Test Method / Conditions | |
| Compression Set (at 22 hours, 175°C) | 11 | % | DIN ISO 815-1 type B method A |
| Density | 1.06 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 650 | % | ISO 37 Type 1 |
| Modulus (at 100 % elongation) | 0.7 | N/mm² | ISO 37 Type 1 |
| Modulus (at 300 % elongation) | 2.3 | N/mm² | ISO 37 Type 1 |
| Shore Hardness A | 32 | — | DIN ISO 48-4 |
| Tear Strength | 20 | N/mm | ASTM D 624 B |
| Tensile Strength | 7 | N/mm² | ISO 37 Type 1 |
| Tension Set | max. 5 | % | ISO 2285 |
| Volume Resistivity | 50 | Ohm-cm | IEC 62631-3-1 |
| Value | Units | Test Method / Conditions | |
| Dynamic Viscosity (Component A, Shear rate 10 s⁻¹) | 435000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Component B, Shear rate 10 s⁻¹) | 360000 | mPa·s | DIN EN ISO 3219 |
| Mix Ratio (A:B) | 1:1 | parts by weight | — |