Features & Benefits
- Materials Features
- Specific Features
Resistant to tracking and erosion.
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Cable Accessories
- Insulators
- Outdoor and indoor use
- Processing
Components A and B are delivered ready to use in drums of 20 and 200 liters capacity. They can be pumped by means of standard metering equipment from these drums and mixing in a static mixer straight into the heated mold. The mixing ratio is 1 : 1. The material fits very well all requirements for manufacturing of large articles with special dosing and metering equipment because of its low viscosity. At room temperature, mixture of A and B components have a pot life of at least three days.
Properties
- Color
- Catalyst Properties
Value Units Test Method / Conditions Dynamic Viscosity (Shear rate 10 s⁻¹) 150000 mPa·s DIN EN ISO 3219 Kick-Off Temperature (A+B) 115 °C - Pot Life (A+B, at 23°C) 3 days - - Cured Properties
Value Units Test Method / Conditions Arc Resistance min. 300 seconds IEC 61621 Density 1.08 g/cm³ DIN EN ISO 1183-1 A Dielectric Strength (1mm sheet) 28 kV/mm IEC 60243-1 Dissipation Factor (tan δ, at 50Hz) 3 x 10⁻³ - IEC 62631-2-1 Elongation (at break) 500 % ISO 37 Type 1 Flammability FV-0 - IEC 60695-11-10 Permittivity (at 50Hz) 2.7 - IEC 62631-2-1 Shore Hardness A 39 - DIN ISO 48-4 Tear Strength 30 N/mm ASTM D 624 B Tensile Strength 8 N/mm² ISO 37 Type 1 Tracking Resistance 1A 4.5 - IEC 60587 Volume Resistivity 5 x 10¹⁵ Ohm-cm IEC 62631-3-1 - Uncured Properties
Value Units Test Method / Conditions Dynamic Viscosity (Component A, Shear rate 10 s⁻¹) 150000 mPa·s DIN EN ISO 3219 Dynamic Viscosity (Component B, Shear rate 10 s⁻¹) 150000 mPa·s DIN EN ISO 3219 Mix Ratio (A:B) 1:1 parts by weight - - Properties
- Ready-to-use, two-component system
- Excellent dielectric properties
- Excellent mechanical properties, especially a high tear strength
- Excellent processing due to its low viscosity, also with suitable mixing and dosing equipment only
- Best suitable for outdoor applications (UV & weathering resistance, excellent hydrophobic properties)
- Note
Cure conditions: 5 min / 165°C and post-cured for 4 h at 200°C.