Knowde Enhanced TDS
Identification & Functionality
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Industrial Additives End Use
- Applications
- Concrete Protection
- Construction Materials
- Fiber Cement Boards
- Hydrophobic Impregnation
- Infrastructure
- Application Details
The work performed (preparing the concrete surface, setting up a reference surface, application and quality control) must follow the applicable regulations
- Concrete should not be impregnated until at least four weeks after it has been produced so that the setting of the cement is not affected.
- New surfaces that are still unsoiled must be cleansed of coarse particles and dust deposits by sweeping or, if necessary, using compressed air. Surfaces already weathered, and those heavily soiled by oil, rubber residue, etc, must first be cleaned using superheated steam or high-pressure water before commencing treatment. It is imperative that the water used be siphoned off immediately to prevent saturation of the concrete.
- Impregnation should always be performed on superficially dry concrete, i.e., when the surface of the concrete appears evenly dry, no more damp patches are visible and the moisture content equilibrium is established. To this end, moisture in the surface zone of the concrete is measured using a suitable technique. The surface-zone moisture content of the concrete (from the surface to a depth of 20 mm) should not exceed 4 wt%.
- Evenly apply the impregnating agent to the building material in two coats, wet-on-wet. The two coats are absolutely essential to prevent the formation of defects in the impregnated surface. Do not allow puddles to form. The impregnating agent is applied by flow coating at reduced pressure. A lambskin roller may be used afterward for more even coverage.
- In the event of unexpected rain, cover surfaces already impregnated and halt all further impregnation.
- SILRES® BS 1701 should never come in direct contact with bitumen. The resistance of insulating materials to SILRES® BS 1701 must be tested on a case-by-case basis for the required temperatures.
SILRES® BS 1701 is recommended for the hydrophobic impregnation and priming of concrete and reinforced concrete in road, bridge and building construction. In addition it is suitable for the hydrophobic treatment of fillers and pigments.
Properties
- Typical Properties
- Properties
SILRES® BS 1701 is characterized by:
- Excellent penetrating power
- No solvents, environmentally compatible
- Low volatility
Treated concrete will have the following permanent properties:
- Dramatic reduction in chloride and water absorption
- No loss in breathability
- Improved durability against freeze-thaw de-icing salt stress
- Enhanced durability
- Provides good adhesion for paints
In the construction material SILRES® BS 1701 reacts with atmospheric moisture and / or the water in the building material’s pores, eliminating alcohol. The active thus substance formed greatly reduces the concrete’s absorbency in the active zone (penetration depth after post treatment), but without blocking any pores or capillaries. The impregnated building material retains very high water-vapor permeability.
| Value | Units | Test Method / Conditions | |
| Boiling Point (at 1013 hPa) | 237 | °C | OECD 103 |
| Density (at 20°C, 1013 hPa) | 0.88 | g/cm³ | DIN 51757 |
| Dynamic Viscosity (at 25°C) | 1.9 | mPa·s | DIN 51562 |
| Flash Point | 42 | °C | ISO 3679 |
| Molecular Weight (Mw) | approx. 276.0 | g/mol | — |
| Silane Content | approx. 99.0 | % | — |
Packaging & Availability
- Country Availability
- Regional Availability
Storage & Handling
- Storage Information
The containers must be protected against sunlight.